Thermal-Mechanical Fatigue and Isothermal Low Cycle Fatigue Fracture Behavior of Powder Metallurgy Superalloy FGH95

ZHANG Guo-dong; LIU Shao-lun; HE Yu-huai; WANG Wu-xiang; ZHONG Bin

Chinese

您当前的位置：

首页 >

文章列表页 >

Thermal-Mechanical Fatigue and Isothermal Low Cycle Fatigue Fracture Behavior of Powder Metallurgy Superalloy FGH95

更新时间：2026-07-07

- Thermal-Mechanical Fatigue and Isothermal Low Cycle Fatigue Fracture Behavior of Powder Metallurgy Superalloy FGH95
- Vol. 20, Issue 1, (2005)
- 作者机构：
  
  北京航空材料研究院,北京,100095
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2005
- 稿件说明：
移动端阅览
ZHANG Guo-dong, LIU Shao-lun, HE Yu-huai, et al. Thermal-Mechanical Fatigue and Isothermal Low Cycle Fatigue Fracture Behavior of Powder Metallurgy Superalloy FGH95[J]. 2005, 20(1).
DOI：

ZHANG Guo-dong, LIU Shao-lun, HE Yu-huai, et al. Thermal-Mechanical Fatigue and Isothermal Low Cycle Fatigue Fracture Behavior of Powder Metallurgy Superalloy FGH95[J]. 2005, 20(1). DOI：

摘要

对粉末冶金盘材料 FGH95进行了同相位

温度循环为 3 5 0℃到 60 0℃的热 /机械疲劳试验和 60 0℃的等温低周疲劳试验。考察了两种载荷波形下材料的循环应力响应行为和高温疲劳断裂机理以及载荷波形对疲劳寿命的影响。研究结果表明 :同相位热 /机械疲劳寿命比上限温度的等温低周疲劳寿命短。该材料在高温应变疲劳的循环应力响应行为与应变水平的大小以及循环载荷波形有关。试样的微观断口分析显示了在高温应变疲劳试验中同时存在疲劳、蠕变和氧化损伤。在同相位热 /机械疲劳载荷下

穿晶 +沿晶断裂为疲劳断裂的主要特征 ;在等温低周疲劳载荷下

裂纹主要为穿晶萌生与扩展

Abstract

High temperature low cycle fatigue behavior of Powder Metallurgy superalloy FGH95 was studied.A basic triangular cycle with a constant temperature of 600℃ and an inphase triangular cycle with maximum and minimum temperature of 350℃ and 600℃ respectively were used for thermal-mechanical fatigue testing.The strain ratio of minimum to maximum strain is -1.0.The influence of the above two loading cycle on cyclic stress response behavior

mechanism of fracture at high temperature and fatigue life was investigated.At same strain amplitude

it was found that the TMF life of in-phase loading form is shorter than that of isothermal low cycle fatigue loading form.High temperature low cycle fatigue behavior of PM superalloy FGH95 depends not only on loading form

but also on magnitude of stain.The microstructure damage behavior of high temperature low cycle fatigue is discussed.The results show that fatigue

creep and oxidation damage always develops simultaneously during low cycle fatigue at high temperature.Fracture is mainly intergranular and transgranular under inphase thermal-mechanical fatigue. The path of crack initiation and growth is transgranular under conditions of isothermal low cycle fatigue.

关键词

Keywords

references

Views

417

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Modeling of low-cycle and creep fatigue life for DZ125 smooth specimens and small-hole components

Experimental analysis of low-cycle and creep fatigue for directionally solidified DZ125 with a hole

Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades

Crystalline Thermo Visco-Plastic Deformation and Damage of Directionally Solidified Turbine Blade

Life Predication of Thermomechanical Fatigue in DS Superalloy DZ125

Related Author

ZHOU Tian-peng

YANG Xiao-guang

SHI Duo-qi

HOU Gui-cang

CONG Pei-hong

QING Hua

JIANG He-fu

Related Institution

School of Jet Propulsion, Beijing University of Aeronautics and Astronautics

Shenyang Aero Engine Research Institute

Shenyang Aeroengine Research Institute, China Aviation Industry Corporation I

College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics

Department of Strength, Gas Turbine Establishment of China

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰