A method for reducing strain-life curve of low cycle fatigue

ZHANG Guo-dong; SU Bin; WANG Hong; ZHONG Bin; XU Chao

Chinese

您当前的位置：

首页 >

文章列表页 >

A method for reducing strain-life curve of low cycle fatigue

更新时间：2026-07-07

- A method for reducing strain-life curve of low cycle fatigue
- Vol. 21, Issue 5, (2006)
- 作者机构：
  
  1. 北京航空材料研究院,北京,100095
  2. 西北工业大学材料科学与工程学院,西安,710072
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2006
- 稿件说明：
移动端阅览
ZHANG Guo-dong, SU Bin, WANG Hong, et al. A method for reducing strain-life curve of low cycle fatigue[J]. 2006, 21(5).
DOI：

ZHANG Guo-dong, SU Bin, WANG Hong, et al. A method for reducing strain-life curve of low cycle fatigue[J]. 2006, 21(5). DOI：

摘要

基于Manson-Coffin方程处理低周应变疲劳应变-寿命曲线

提出了一种在短寿命区用低周应变疲劳试验数据

长寿命区（5000周50000周）用高周疲劳试验数据联合确定材料的高温低周应变疲劳应变-寿命曲线的方法。联合处理方法的应用将不再需要进行应变控制的长寿命小应变的疲劳试验

节约了试验经费

缩短了试验周期。用GH141合金760℃的低周应变疲劳和高周疲劳数据对该方法进行了验证

验证结果发现:联合处理方法和单纯的Manson-Coffin方程处理得到的应变-寿命曲线吻合很好。联合处理方法可以用来确定高温低周应变疲劳应变-寿命曲线。

Abstract

Based on Manson-Coffin equations of low cycle fatigue(LCF) under strain controlled to acquire strain-life curve

a new technique for determining strain-life curve of LCF is developed.When fatigue life is shorter than 5000 cycles

experimental data of LCF under strain controlled are used.But when fatigue life is longer than 5000 cycles

experimental data of high cycle fatigue(HCF) under stress controlled are employed.This new method of combining LCF with HCF allows to avoid long fatigue life with small strain test under strain controlled

thus test expenses may be saved and test time shortened.Experimental data of LCF and HCF are reduced by new method for superalloy GH141

at temperature 760℃. Strain-life curves obtained by simply Manson-Coffin equation and by new method are in good agreement.The new method combining by LCF with HCF can be used to get strain-life curve of LCF.

关键词

Keywords

references

Views

442

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Experiment of effect of shot peening strengthening on TC11 alloy simulation blade's HCF life

Experimental analysis of low-cycle and creep fatigue for directionally solidified DZ125 with a hole

Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades

Effect of Elastic Modulus on Parameter of Low Cycle Fatigue Performance

A thermo-mechanical fatigue life assessment method for single crystal turbine blades

Related Author

WANG Mei

LU Shan

GU Yuan-xing

LIU Liang

ZHANG Huan

ZHOU Tian-peng

YANG Xiao-guang

HOU Gui-cang

Related Institution

School of Power and Energy, Northwest Polytechnical University

China Gas Turbine Establishment, Aviation Industry Corporation of China

School of Jet Propulsion, Beijing University of Aeronautics and Astronautics

Shenyang Aeroengine Research Institute, China Aviation Industry Corporation I

College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰