Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades

QING Hua; JIANG He-fu; WEN Wei-dong; WU Chang-bo; SUN Jing-guo

Chinese

您当前的位置：

首页 >

文章列表页 >

Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades

更新时间：2026-07-07

- Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades
- Vol. 22, Issue 5, (2007)
- 作者机构：
  
  1. 南京航空航天大学能源与动力学院,南京,210016
  2. 中国燃气涡轮研究院强度研究室,成都,610500
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2007
- 稿件说明：
移动端阅览
QING Hua, JIANG He-fu, WEN Wei-dong, et al. Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades[J]. 2007, 22(5).
DOI：

QING Hua, JIANG He-fu, WEN Wei-dong, et al. Study on the creep behavior of model specimens of nickel-based single crystal air-cooled blades[J]. 2007, 22(5). DOI：

摘要

对带孔和不带孔的某第二代镍基单晶合金平板试样进行了蠕变性能试验研究与有限元对比计算.高温蠕变试验表明

平板试样的晶体取向和是否开孔对蠕变寿命有明显的影响.气膜孔导致蠕变寿命的降低

对[001]取向的影响大于[111]取向.在高温低应力条件下

[001]取向的蠕变性能要优于[111]取向.有限元分析结果表明

气膜孔改变了试样中的应力分布

在孔附近产生了高应力

导致模拟试验蠕变寿命的降低.有限元计算蠕变持久寿命与试验结果吻合

说明采用基于分切应力的蠕变持久寿命计算模型是合理的.

Abstract

Plate specimens were used to model turbine blades with cooling holes.Experimental and numerical study on the creep behavior of a second generation nickel-based single crystal alloy has been performed with these model specimens.The results of creep test at high temperature show that crystallographic orientations and cooling holes have noticeable influence on the creep life.Compared with that of the specimen without cooling holes

the creep life of specimen with cooling holes is lower for both and orientations.The cooling holes have larger influence on the creep life of orientation than that of orientation.The creep behavior under high temperature and low stress conditions of orientation is better than that of orientation.The finite element analysis(FEA) results reveal that the cooling holes change the stress distribution in the specimen and cause stress concentration near the holes

which results in the decrease of creep life.As the creep life obtained from FEA is accordant to the experimental result

it is reasonable to calculate the creep life using the simulation model based on the resolved slip stress.

关键词

Keywords

references

Views

459

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Experimental analysis of low-cycle and creep fatigue for directionally solidified DZ125 with a hole

Life prediction of cooling passage for reusable liquid rocket engine

Modeling of low-cycle and creep fatigue life for DZ125 smooth specimens and small-hole components

A method for reducing strain-life curve of low cycle fatigue

Effect of Elastic Modulus on Parameter of Low Cycle Fatigue Performance

Related Author

ZHOU Tian-peng

YANG Xiao-guang

HOU Gui-cang

SHI Duo-qi

CONG Pei-hong

YANG Jin-hui

CHEN Tao

JIN Ping

Related Institution

School of Jet Propulsion, Beijing University of Aeronautics and Astronautics

Shenyang Aeroengine Research Institute, China Aviation Industry Corporation I

School of Astronautics, Beijing University of Aeronautics and Astronautics

Shenyang Aero Engine Research Institute

Beijing Institute of Aeronautical Materials

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰