New characteristics of fatigue-creep tests on serration of turbine blades

更新时间：2026-07-07

- New characteristics of fatigue-creep tests on serration of turbine blades
- Vol. 22, Issue 3, (2007)
- 作者机构：
  
  北京航空航天大学能源与动力工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2007
- 稿件说明：
移动端阅览
SUN Rui-jie, YAN Xiao-jun. New characteristics of fatigue-creep tests on serration of turbine blades[J]. 2007, 22(3).
DOI：

SUN Rui-jie, YAN Xiao-jun. New characteristics of fatigue-creep tests on serration of turbine blades[J]. 2007, 22(3). DOI：

摘要

在某型航空发动机涡轮叶片的低周疲劳试验中发现

叶片疲劳/蠕变试验寿命高于纯疲劳试验寿命

为探究这一现象的原因

对此展开相关的理论计算和分析.研究表明:试验条件较好地模拟了叶片的实际工作条件

该涡轮叶片的损伤以疲劳损伤为主

相对于真实涡轮叶片的纯疲劳试验

在疲劳/蠕变试验条件下

其考核部位(榫齿)出现了较大的应力松弛

故而使得叶片疲劳/蠕变寿命高于纯疲劳寿命.研究结果对于保证发动机安全工作、提高飞行可靠性、以及发展高温构件的疲劳试验技术有重要意义.

Abstract

The fatigue-creep life was found to be longer than the fatigue life from the Low Cycle Fatigue experiment of turbine blade of an aeroengine.The relevant theoretical calculation and analysis were then carried out to provide a further insight into such phenomenon.The research shows that: the actual working conditions of blades were well simulated in the experimental conditions

indicating that the damage of blade was mainly attributable to fatigue damage.As compared with pure fatigue test of real turbine blade

stress relaxation occurred at the key section(serration) under fatigue-creep test conditions

showing that fatigue/creep life of blade was longer than fatigue life.The research results play a key role in ensuring the safety of engines

improving the flight reliability and developing fatigue test techniques of high-temperature components.

关键词

Keywords

references

Views

510

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Turbine blade displacement transfer based on mesh regeneration method

Displacement transfer with the mesh deformation method in multidisciplinary optimization of turbine blades

Experimental research on heat transfer of "impingement/effusion" double-plate configuration in rotating state

Influence of aerodynamic parameters on film cooling effectiveness on the vane leading edge

Influence of pin fin on the convective heat transfer characteristics of turbine blade trailing edge

Related Author

LI Li-zhou

WANG Jing-chao

LU Zhen-zhou

YUE Zhu-feng

HAN Yong-zhi

XU Lei

CHANG Hai-ping

PAN Jin-dong

Related Institution

School of Aeronautics, Northwestern Polytechnincal University

School of Mechanics Civil Engineering and Architecture, Northwestern Polytechnincal University

College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics

School of Power and Energy,Northwestern Polytechnical University

China Aviation Powerplant Research Institute

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰