Application research of damage dynamics for low cycle fatigue test

ZHANG Guo-dong; YU Hui-chen; HE Yu-huai; SU Bin

Chinese

您当前的位置：

首页 >

文章列表页 >

Application research of damage dynamics for low cycle fatigue test

更新时间：2026-07-07

- Application research of damage dynamics for low cycle fatigue test
- Vol. 22, Issue 9, (2007)
- 作者机构：
  
  中国航空工业第一集团公司北京航空材料研究院,北京,100095
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2007
- 稿件说明：
移动端阅览
ZHANG Guo-dong, YU Hui-chen, HE Yu-huai, et al. Application research of damage dynamics for low cycle fatigue test[J]. 2007, 22(9).
DOI：

ZHANG Guo-dong, YU Hui-chen, HE Yu-huai, et al. Application research of damage dynamics for low cycle fatigue test[J]. 2007, 22(9). DOI：

摘要

考察了低周疲劳过程中的弹性模量和应力随循环次数的变化.研究表明:可以用弹性模量和应力的变化来反映材料的低周疲劳损伤过程.对没有明显循环稳定阶段并表现为循环软化响应行为的材料

不适合用应力的变化来定量的反映材料低周疲劳的损伤过程.用弹性模量随循环次数的演化关系得到了不同应变水平下材料的疲劳裂纹萌生寿命

并用三参数幂函数方程对应变与疲劳裂纹萌生寿命进行了拟合处理

得到了应变与疲劳裂纹萌生寿命方程.

Abstract

The change of elastic modulus and stress associated with fatigue cyclic number was investigated during low cycle fatigue.The research shows that

the low cycle fatigue damage can be determined by the change of elastic modulus and stress.For the materials

which have no cyclic steady stage but exhibit cyclic softening

this method isn't suitable to determine the low cycle fatigue damage with the change of stress.The fatigue crack initiation life was acquired by the change of elastic modulus under different strain levels

so the relationship between strain and fatigue crack initiation life was determined by three parameters power equation.

关键词

Keywords

references

Views

435

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Design of simulated specimen for low-cycle fatigue of turbine engine disk

Research on impact damage of T300/BMP-316 composite laminates

Effect of Elastic Modulus on Parameter of Low Cycle Fatigue Performance

Tensile Behavior of a Single Crystal Ni-Base Superalloy at Different Temperatures

Applied Investigation of Chaboche’s Unified Visco-Plastic Constitutive Model of Coupled Creep Damage

Related Author

LIU Ting-yi

GENG Rui

ZHANG Jun-feng

WEN Wei-dong

CUI Hai-po

XU Ying

ZHANG Guo-dong

SU Bin

Related Institution

School of Jet Propulsion, Beijing University of Aeronautics and Astronautics

Shenyang Aeroengine Research Institute, China Aviation Industry Corporation Ⅰ

College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics

Beijing Institute of Aeronautical Materials

School of Material Science and Engineering,Northwestern Polytechnical University

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰