Post-impact compressive strength experiment of T300/BMP316 composite laminates

CUI Hai-po; WEN Wei-dong

Chinese

您当前的位置：

首页 >

文章列表页 >

Post-impact compressive strength experiment of T300/BMP316 composite laminates

更新时间：2026-07-07

- Post-impact compressive strength experiment of T300/BMP316 composite laminates
- Vol. 23, Issue 11, (2008)
- 作者机构：
  
  1. 上海理工大学医疗器械与食品学院,上海,200093
  2. 南京航空航天大学能源与动力学院,南京,210016
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2008
- 稿件说明：
移动端阅览
CUI Hai-po, WEN Wei-dong. Post-impact compressive strength experiment of T300/BMP316 composite laminates[J]. 2008, 23(11).
DOI：

CUI Hai-po, WEN Wei-dong. Post-impact compressive strength experiment of T300/BMP316 composite laminates[J]. 2008, 23(11). DOI：

摘要

对两种不同铺层参数的T300/BMP316复合材料层合板进行了冲击后的剩余压缩强度试验研究.结果表明

虽然随着冲击能量的增加

层合板的剩余压缩强度逐渐降低

但二者之间不满足线性关系;不同铺层参数对层合板冲击损伤投影图形的长轴方向有一定的影响

但对冲击损伤投影面积大小几乎没有影响;层合板的剩余压缩强度与冲击损伤投影面积的大小没有直接关系.

Abstract

Experiment study on impact damage and residual compressive strength had been done on T300/BMP316 composite laminates with different layer parameters.The results show that although the residual compressive strength gradually decreased with the increasing impact energy

there is no linear relationship between of them.The layer parameters has effect on the long-axis direction of impact damage figure

but hasn't influence on the impact damage area.The residual compressive strength has no direct relationship with the impact damage area.

关键词

Keywords

references

Views

447

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Experimental research on impact damage and residual tensile strength of composite laminates

Effect analysis of delamination damage on the residual strength of notched composite laminates

Failure analysis and prediction on the open-hole tensionof domestic carbon fiber composite

Influence of different impact energies on damage and residual strength of laminates

Principle experiments on two phase pulse detonation turbine engine

Related Author

CUI Hai-po

WEN Wei-dong

XU Ying

XIAO Meng-li

ZHANG Yong-bo

WANG Zhi-hua

FU Hui-min

YANG Xin

Related Institution

College of Energy and Power Engineering, Nanjing University of Aeronautics and Astronautics

Institute of Medical Device, University of Shanghai for Science and Technology

Research Center of Small Sample Technology, Beijing University of Aeronautics and Astronautics

Shanghai Institute for Minimally Invasive Therapy, University of Shanghai for Science and Technology

School of Power and Energy,Northwestern Polytechnical University

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰