Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures

XIE Ruo-ze; ZHANG Fang-ju; DENG Zhi-fang; LU Zi-xing

Chinese

您当前的位置：

首页 >

文章列表页 >

Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures

更新时间：2026-07-07

- Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures
- Vol. 24, Issue 4, (2009)
- 作者机构：
  
  1. 中国工程物理研究院结构力学研究所,绵阳,621900
  2. 北京航空航天大学固体力学所,北京,100191
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2009
- 稿件说明：
移动端阅览
XIE Ruo-ze, ZHANG Fang-ju, DENG Zhi-fang, et al. Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures[J]. 2009, 24(4).
DOI：

XIE Ruo-ze, ZHANG Fang-ju, DENG Zhi-fang, et al. Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures[J]. 2009, 24(4). DOI：

摘要

利用配备自动组装系统和高温加热系统的直径为 ф5 mm的Hopkinson压杆

对温度在20℃～400℃、应变率在(5～14)×103s-1范围内LY12铝的动态压缩力学性能进行了实验研究.实验中采用波形整形技术

有效地消除了入射波的高频振荡

提高了测试精度.实验结果表明:当实验温度低于200℃时

温度的影响较小

而高于200℃时

材料的温度软化效应将十分明显

且随着温度的升高

流动应力逐步降低;LY12铝的性质接近于线性硬化材料

随温度的升高

其硬化模量逐步降低;在(5～14)×103s-1应变率范围内

LY12铝的动态压缩性能的应变率效应并不明显.

Abstract

The dynamic mechanical properties of LY12 aluminum were studied experimentally by Hopkinson Bar of diameter 5mm with an automatic assembling system and heating system

within the range of temperature from 20℃ to 400℃ and strain-rate from 5×103s-1 to 1.4×104s-1.In the experiments

a shaper was used to eliminate the oscillation of high frequency in the incident signal and to improve the experimental precision of bar system.The experimental results show that the effect of temperature on dynamic properties of LY12 is not great at temperature lower than 200℃;on the contrary

the thermal softening effect is obvious at temperature higher than 200℃

exhibiting the decrease of flow stresses and linear harden modulus with increase of temperature

which is similar to linear harden materials.From the experiments

the dynamic properties of LY12 don't show strong sensitivity to the strain rates.

关键词

Keywords

references

Views

437

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Wear life analysis of angular contact ball bearing in high temperature environment

Strength prediction of 3-D four directional C/C composites by high temperature and oxidation environment

Comparative experiment of hightemperature crack propagation behaviors for four kinds of typical titanium alloys

Thermal protection performances of metallic honeycomb panel structure at transient thermal shock environment

Friction/wear behaviors and predication of graphite seal material under high temperature

Related Author

Zhengjie HAN

Yufei WANG

Hongliang LI

Sier DENG

Rongjun NIU

徐颖

张宏建

崔海涛

Related Institution

Special Bearing Business Department， Luoyang Bearing Research Institute Company，Limited

School of Mechatronics Engineering， Henan University of Science and Technology

南京航空航天大学能源与动力学院

北京航空航天大学交通科学与工程学院

中国航空发动机集团有限公司北京航空材料研究院

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰