- Laser shock peening on vibration fatigue behavior of compressor blade
- Vol. 26, Issue 7, (2011)
- 作者机构：
  
  空军工程大学工程学院,西安,710038
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Published：2011
- 稿件说明：
移动端阅览
HE Wei-feng, LI Ying-hong, LI Wei, et al. Laser shock peening on vibration fatigue behavior of compressor blade[J]. 2011, 26(7).
DOI：

HE Wei-feng, LI Ying-hong, LI Wei, et al. Laser shock peening on vibration fatigue behavior of compressor blade[J]. 2011, 26(7). DOI：

摘要

根据1Cr11Ni2W2MoV不锈钢材料性能

确定了激光冲击强化参数;并通过标准试片疲劳试验

验证了该参数条件下激光冲击强化提高不锈钢材料振动疲劳寿命的有效性.设计了不锈钢叶片振动疲劳试验

确定了叶片冲击强化部位和方式

对强化叶片进行了型面检查、一阶弯曲振动疲劳试验和强化机理研究.结果表明:激光冲击强化后的叶片各个截面尺寸在设计范围之内

强化后叶片的应力-循环次数(S-N)曲线往上移动

提高了叶片的疲劳强度

在660MPa应力水平下

叶片的振动中值疲劳寿命提高70%;激光冲击强化引起的残余应力和表层微观组织变化是疲劳强度提高的主要原因.

Abstract

According to the mechanical performance of the 1Cr11Ni2W2MoV stainless steel

the technical parameters of laser shock peening(LSP) were determined. The standard coupons with/without LSP were tested for examining the fatigue performance. It proves that LSP

with the selected parameters

can improve the stainless steel's vibration fatigue life remarkably. From the experiment results of coupons

the vibration fatigue experiment for the compressor blade in one certain aero-engine was designed according to the structure and loads of the blade. The treated zone was designed on the surface where the vibration stress is the most severe. In order to avoid macroscopical deformation

the blades were treated on both sides simultaneously. This confirms that different section parameters after LSP on the blade are within the range of design requests. The vibration fatigue results indicate that the S-N (stress-number of cycles) curve with LSP moves up as compared with that one without LSP. When the max vibratory stress was about 660MPa

the blade fatigue life with LSP was prolonged for 70%. Finally

the reasons were analyzed from the residual compressive stress and micro structure after LSP.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Numerical simulation on laser shock peening of TC4 titanium alloy

Improving fatigue performance of titanium alloy simulated-blade subjected to foreign object damage by laser shock peening

Effects on structure and mechanical properties of TC11 titanium alloy by laser shock peening

Effect of different shot peening intensities on fatigue resistance of TC17 titanium alloy

Analysis of dynamic coupling characteristics of high speed angular contact ball bearing⁃rigid rotor system under different working conditions

Related Author

WANG Bohan

CHENG Li

DING Junliang

CUI Wenbin

WANG Changkai

LI Dongchun

NIE Xiangfan

WEI Chen

Related Institution

Aeronautics Engineering College,Air Force Engineering University

Collaborative Innovation Center for Advanced Aero-Engines

Science and Technology on Plasma Dynamics Laboratory, Aeronautics and Astronautics Engineering College, Air Force Engineering University

School of Mechanical Engineering, Xi'an Jiaotong University

Shenyang Engine Research Institute，Aero Engine Corporation of China

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰