Microstructure of Semi-solid AZ31B Magnesium Alloy Through Strain-induced Meltactivation Method

更新时间：2026-07-10

- Microstructure of Semi-solid AZ31B Magnesium Alloy Through Strain-induced Meltactivation Method
- Vol. 14, Issue 1, Pages: 67-71(2009)
- 作者机构：
  
  1. 哈尔滨理工大学材料科学与工程学院
  2. 东京大学生产技术研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG146.22
- Published：2009
- 稿件说明：
移动端阅览
JI Ze-sheng, SUGIYAMA Sumio, YANAGIMOYO Jun. Microstructure of Semi-solid AZ31B Magnesium Alloy Through Strain-induced Meltactivation Method[J]. 2009, 14(1): 67-71.
DOI：

JI Ze-sheng, SUGIYAMA Sumio, YANAGIMOYO Jun. Microstructure of Semi-solid AZ31B Magnesium Alloy Through Strain-induced Meltactivation Method[J]. 2009, 14(1): 67-71. DOI：

摘要

采用AZ31B镁合金挤出材

在573K进行28%~30%预变形加工

然后在863~893K经过不同保温时间进行等温球化处理

观察了试样不同区域的组织

考察了温度及保温时间对组织的影响

得到了具有圆整固相颗粒的半固态组织.实验结果表明:适当提高球化处理温度

有利于加速球化过程

以获得细小圆整半固态组织;延长保温时间固相分数降低

但幅度不大

并发生颗粒不规则化;在同一个试样上

由于部位不同

变形程度不同

所得半固态材料的固相率不同.讨论了半固态组织的形成机理

分析认为预变形后

半固态组织形成过程包括再结晶、晶粒长大阶段

受溶质、空位扩散控制的半固态组织形成阶段

受液—固界面张力作用的固相颗粒圆整化阶段.开始形成半固态组织阶段

扩散占主导地位

在进一步球化过程中

界面张力占主导地位.

Abstract

【英文摘要】 A semi-solid microstructure of AZ31B magnesium alloy containing spherical solid particles was studied.This material was subjected to a series of spheroidizing treatments for various holding times at 863~893K after being compressed by 28%~30% in length at 573K.The effects of heating temperature and holding time on microstructures were studied.It was found that increasing the heating temperature could accelerate the spheroidizing process

resulting in small spherical semi-solid microstructures.With a longer ho...

关键词

Keywords

references

Views

2314

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on Fatigue Behaviour of AZ31B Magnesium Alloy adoping Screw-type Notch Sample

Health Prediction of Electric Meter Calibration Lines by Combining Memory Network and Attention

Cooperative Optimal Scheduling Strategy of Agent Reinforcement Learning based on Source-load Characteristic Analysis

Mechanism and Improvement of Electric Ablation of Buffer Layer of High Voltage Corrugated Aluminum Sheathed Cable

Research on Insulator Defect Recognition in Substations

Related Author

WANG Hai-bo

LI Dong-hua

WU Shu-yan

WANG Yong-chao

Related Institution

哈尔滨理工大学建筑工程学院

佳木斯大学材料科学与工程学院

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰