Ni-P nanoglass prepared by multi-phase pulsed electrodeposition

Chunyu Guo; Yini Fang; Bin Wu; Si Lan; Guo Peng; Xun-li Wang; Horst Hahn; Herbert Gleiter; Tao Feng

doi:10.1080/21663831.2016.1264495

Chinese

您当前的位置：

首页 >

文章列表页 >

Ni-P nanoglass prepared by multi-phase pulsed electrodeposition

Original Report | 更新时间：2026-08-19

- Ni-P nanoglass prepared by multi-phase pulsed electrodeposition
- Materials Research Letters Vol. 5, Issue 5, Pages: 293-299(2017)
- 作者机构：
  
  1. Herbert Gleiter Institute of Nanoscience Nanjing University of Science & Technology
  2. Department of Physics and Materials Science City University of Hong Kong
  3. Herbert Gleiter Institute of Nanoscience Nanjing University of Science & Technology Nanjing People's Republic of China
  4. Institute of Nanotechnology Karlsruhe Institute of Technology
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2016.1264495
  CLC：
- Online First：12 December 2016，
  
  Published：2017
- 稿件说明：
移动端阅览
Chunyu Guo, Yini Fang, Bin Wu, et al. Ni-P nanoglass prepared by multi-phase pulsed electrodeposition[J]. Materials Research Letters, 2017, 5(5): 293-299.
DOI：

Chunyu Guo, Yini Fang, Bin Wu, et al. Ni-P nanoglass prepared by multi-phase pulsed electrodeposition[J]. Materials Research Letters, 2017, 5(5): 293-299. DOI： 10.1080/21663831.2016.1264495.

摘要

Abstract

BSTRACTNi-P nanoglass consisting of nanometer-sized amorphous grains separated by amorphous interfaces was prepared by a specially designed multi-phase pulsed electrodeposition technique. The microstructure of the deposited Ni-P nanoglass was confirmed by X-ray diffraction

high-resolution transmission electron microscopy

small-angle X-ray scattering

and X-ray photoelectron spectroscopy. The formation of the Ni-P nanoglass

which is characterized by inhomogeneities on the nanometer length scale

is achieved via proper control of the rate of cluster formation and cluster growth by a multi-phase pulsed electrodeposition process.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Breaking mixture rule of strength and ductility by interface induced nano-scale heterostructure in TA1/304 composites

Bi addition increases strength and strain-softening behavior in SAC305

Mechanism of the reversed yield asymmetry in a strong-textured Mg-RE alloy at room temperature

Microstructural heterogeneity enabled balance of room- and high-temperature properties in high-volume intermetallics reinforced aluminum alloys

Achieving uniform and wide phase transformation hysteresis in twin-wire arc additive manufactured NiTiNb alloy

Related Author

Yuhui Li

Kai Yao

Zhixin Wang

Baoli He

Boyang Li

Chunguang Shen

Lingling Zhang

Shijian Zheng

Related Institution

State Key Laboratory of High-Performance Roll Materials and Composite Forming School of Materials Science and Engineering Hebei University of Technology

School of Materials Engineering Purdue University West Lafayette

a School of Materials Engineering Shanxi College of Technology

b School of Materials Science and Engineering Taiyuan University of Science and Technology

c State Key Laboratory for Mechanical Behavior of Materials Xi’an Jiaotong University

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰