Strengthening mechanisms of cold worked MP35N alloy during aging treatment

CHEN Yulai; YANG Dongyan; LI Jingyuan; ZHANG Yuan

doi:10.11918/j.issn.0367-6234.201507037

Chinese

您当前的位置：

首页 >

文章列表页 >

Strengthening mechanisms of cold worked MP35N alloy during aging treatment

更新时间：2026-10-19

- Strengthening mechanisms of cold worked MP35N alloy during aging treatment
- Vol. 49, Issue 5, Pages: 2017-5(2017)
- 作者机构：
  
  1. 北京科技大学冶金工程研究院,北京,100083
  2. 北京科技大学材料科学与工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：10.11918/j.issn.0367-6234.201507037
  CLC： TG135.1
- Published：2017
- 稿件说明：
移动端阅览
CHEN Yulai, YANG Dongyan, LI Jingyuan, et al. Strengthening mechanisms of cold worked MP35N alloy during aging treatment[J]. 2017, 49(5): 2017-5.
DOI：

CHEN Yulai, YANG Dongyan, LI Jingyuan, et al. Strengthening mechanisms of cold worked MP35N alloy during aging treatment[J]. 2017, 49(5): 2017-5. DOI： 10.11918/j.issn.0367-6234.201507037.

摘要

为研究MP35N合金时效强化规律及机制，对MP35N合金进行84.18%的冷轧变形后，进行时效处理研究.在万能拉伸机上进行力学性能测试，用OM、SEM、TEM和EDS进行组织分析和微观成分测试.实验结果表明：在500 ℃时效4 h时，显微硬度达到最大值704.26 HV，抗拉强度为2641.16 MPa，与冷轧态相比，分别提高了30.44%和37.41%；该合金经时效后冷轧撕裂孔洞愈合，在400 ℃时效后出现了由3~4个厚度为3 nm左右的细小孪晶组成的“孪晶簇”；温度升高到500 ℃，孪晶尺寸变大、交错，“孪晶簇”消失.未发现Mo原子在孪晶处处偏聚，时效过程中形成的纳米级片状孪晶起到主要的强化作用.

Abstract

The strengthening mechanism during aging treatment after 84.18% cold rolling of MP35N alloy was performed in this study. Mechanical properties were tested on universal tensile testing machine and the microstructures were analyzed by OM

SEM

TEM and EDS. The results show that the maximum micro-hardness

704.26 HV

was obtained when MP35N alloy was aged at 500 ℃ for 4 h

at which state the tensile strength was 2641.16 MPa. The two values increased by 30.44% and 37.41% over cold rolling state respectively. Tear holes which formed during cold forming healed after aging and the TEM result revealed that the thin "twin cluster" consisting of 3 to 4 fine twins which thickness about 3 nm appeared after aged at 400 ℃. When the temperature increased to 500 ℃

twin size became larger

staggered and then "twin cluster" disappeared. The EDS results shows there is no obvious concentration of Mo atom occurred in the twins. Nano flake twins formed during aging treatment play a major role in strengthening.

关键词

Keywords

references

Views

633

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Intelligent prediction method for cold rolling motor power based on data-driven and mechanism coupling

Influence of lubrication film thickness on transfer of surface topography at cold rolling interface

Generative face detection algorithm based on multi-scale fusion and receptive field enhancement

Speech-to-image generation method based on a single-stage framework

Incremental intrusion detection mechanism considering cost-sensitive

Related Author

CAO Lei

DONG Zishuo

LI Xiaohua

LI Xu

ZHANG Dianhua

XU Dong

YANG Quan

WANG Xiaochen

Related Institution

（State Key Laboratory of Rolling and Automation (Northeastern University),,）

国家板带生产先进装备工程技术研究中心(北京科技大学)

National Engineering Research Center of Flat Rolling Equipment（ University of Science and Technology Beijing）

北京科技大学机械工程学院

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰