Study on the springback and quality of S355J2W steel in resistance heating bending

FANG Hui; WANG Guofeng; LIU Siyu

doi:10.11918/j.issn.0367-6234.201805117

Chinese

您当前的位置：

首页 >

文章列表页 >

Study on the springback and quality of S355J2W steel in resistance heating bending

更新时间：2026-10-19

- Study on the springback and quality of S355J2W steel in resistance heating bending
- Vol. 50, Issue 11, Pages: 10-16(2018)
- 作者机构：
  
  哈尔滨工业大学金属精密热加工国家级重点实验室,哈尔滨,150001
- 作者简介：
- 基金信息：
- DOI：10.11918/j.issn.0367-6234.201805117
  CLC： TG306
- Published：2018
- 稿件说明：
移动端阅览
FANG Hui, WANG Guofeng, LIU Siyu. Study on the springback and quality of S355J2W steel in resistance heating bending[J]. 2018, 50(11): 10-16.
DOI：

FANG Hui, WANG Guofeng, LIU Siyu. Study on the springback and quality of S355J2W steel in resistance heating bending[J]. 2018, 50(11): 10-16. DOI： 10.11918/j.issn.0367-6234.201805117.

摘要

为研究S355J2W高强钢板自阻加热弯曲成形过程中电流密度对回弹的影响及成形件的质量

设计了自阻加热V形弯曲试验和自阻加热几字形弯曲试验

通过改变自阻加热时加载的电流密度大小对成形后零件的回弹现象进行研究.根据试验结果

选择成形精度最高、回弹现象最小的几字形零件进行质量分析

并将其与室温成形的几字形零件进行对比

从而研究自阻加热弯曲成形工艺的优势.将所选取的两个几字形零件分别划分为9个不同的区域

对不同区域的试件进行显微组织观察与力学性能测试

将单向拉伸试验、冲击落锤试验与显微硬度的测试结果作为评价成形件质量的标准

同时将两个零件在力学性能上的差异与显微组织观察的结果联系起来.结果表明:随着电流密度的增大

S355J2W钢自阻加热弯曲成形过程中的回弹得到改善; 相比于室温成形的几字形零件

采用自阻加热弯曲成形工艺可以很大程度地改善回弹现象; 并且自阻加热成形件的组织更加均匀

其力学性能指标

如抗拉强度

延伸率

冲击韧性和显微硬度也有所提高.

Abstract

In order to investigate the influence of the current density on the springback and quality of S355J2W steel parts formed by resistance heating bending

the V-shaped and cap-shaped resistance heating bending experiments were designed.The springback of steel parts after forming was studied by varying current densities in resistance heating.According to the test results

the quality of the parts with the highest forming accuracy and the smallest springback were selected to compare with the parts formed at room temperature to study the advantage of resistance heating bending.The selected two parts were divided into 9 different regions.The microstructure and mechanical properties of these regions

such as strength

hardness

elongation

and impact toughness were used as the standard to evaluate the quality of the formed parts.Moreover

the differences in mechanical properties of the two parts were explained by the results of microstructural observation.The results showed that the springback of S355J2W steel in resistance heating bending was improved with the increase current density.Compared to the parts formed at room temperature

resistance heating bending process can greatly improve the springback and quality.At the same time

the mechanical properties were also improved in resistance heating bending.

关键词

Keywords

references

Views

495

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Springback prediction of DP980 steel considering nonlinear elastic modulus in cold roll forming

Dynamic liquid level prediction using virtual samples generated by FD-constrained transfer

Efficient time series forecasting model for feature selection

Estimation method of heterogeneous treatment effect with multiple treatment

Cascade iterative refinement of Dunhuang mural image inpainting

Related Author

LIU Xiaoli

CAO Jianguo

CHAI Xueting

LIU Jiang

CHENG Jiaojiao

ZHAO Rongguo

Related Institution

School of Mechanical Engineering, University of Science and Technology Beijing

National Engineering Research Center of Flat Rolling Equipment(University of Science and Technology Beijing)

Jiangsu Durable Machinery Co.

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰