Effect of foreign object damage at different impact angles onhigh cycle fatigue strength of TC4 titanium alloys

BAO Zhen-qiang; HU Xu-teng; SONG Ying-dong

doi:10.13224/j.cnki.jasp.2015.09.023

Chinese

您当前的位置：

首页 >

文章列表页 >

Effect of foreign object damage at different impact angles onhigh cycle fatigue strength of TC4 titanium alloys

更新时间：2026-07-07

- Effect of foreign object damage at different impact angles onhigh cycle fatigue strength of TC4 titanium alloys
- Vol. 30, Issue 9, Pages: 2226-2233(2015)
- 作者机构：
  
  1. 南京航空航天大学能源与动力学院江苏省航空动力系统重点实验室,南京,210016
  2. 南京航空航天大学机械结构力学及控制国家重点实验室,南京,210016
- 作者简介：
- 基金信息：
- DOI：10.13224/j.cnki.jasp.2015.09.023
  CLC：
- Published：2015
- 稿件说明：
移动端阅览
包珍强, 胡绪腾, 宋迎东. 不同冲击角度外物损伤对TC4钛合金高循环疲劳强度的影响[J]. 航空动力学报, 2015, 30(9): 2226-2233.

doi: 10.13224/j.cnki.jasp.2015.09.023
包珍强, 胡绪腾, 宋迎东. 不同冲击角度外物损伤对TC4钛合金高循环疲劳强度的影响[J]. 航空动力学报, 2015, 30(9): 2226-2233. DOI： 10.13224/j.cnki.jasp.2015.09.023.

doi: 10.13224/j.cnki.jasp.2015.09.023 DOI：

摘要

基于空气炮冲击试验装置在不同冲击角度下进行了TC4钛合金平板试件的外物损伤模拟试验

采用逐级加载试验方法测试获得了光滑和冲击损伤试件的高循环疲劳(high cycle fatigue

HCF)强度

研究了冲击角度、冲击位置以及冲击损伤宏观几何尺寸与HCF强度的关系.结果表明:不同冲击角度下的损伤对HCF强度的影响程度不同.冲击损伤在试件边缘时

30°冲击使试件HCF强度的下降幅度最大;冲击损伤在试件表面时

60°冲击使试件HCF强度的下降幅度最大.试件边缘产生的缺口使HCF强度的下降幅度一般大于试件表面产生弹坑的影响.但在60°冲击时

冲击缺口损伤的影响要小于冲击弹坑损伤的影响.冲击损伤宏观几何尺寸一定程度上可以表征损伤试件HCF强度下降的严重程度.

Abstract

Based on the air-gun impact test device

the foreign object damage (FOD) simulation test of TC4 titanium alloy plate specimens was conducted at different impact angles. The high cycle fatigue (HCF) strength of smooth and impact damage samples was obtained with the step-test method. The relationship among the impact angles

impact positions

macroscopic geometry of impact damage and HCF strength of the damaged samples was studied. Results show that

the effect of impact damages on the HCF strength at different impact angles is not the same. When the impact damage appears at the edge of sample

the maximum decrease of HCF strength occurs in the impaction of 30°; while the impact damages appear at the middle of sample

the maximum decrease of HCF strength occurs in the impaction of 60°. In most cases

impact notches at the samples' edge compared to impact pits at the sample's intermediate surface have a more seriously effect on the HCF strength. However

at the impaction of 60°

the impact pit damage has a more serious effect. The geometry of the impact damage to a certain extent can characterize the changes of the HCF strength severity of damaged sample.

关键词

Keywords

references

Views

568

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Essential characteristic of foreign object damage tolerance design for airfoils in aeroengine and development of design criteria

Numerical simulation on laser shock peening of TC4 titanium alloy

Numerical analysis on residual stress of foreign object damage on the leading edge of titanium alloy blade

Electric field and flow field of LPES surface strengthening of titanium alloy gear

Effect of dent-type foreign object damage on fatigue strength of TC4 material

Related Author

SONG Ying-dong

HU Xu-teng

LI Dongchun

WANG Changkai

CUI Wenbin

DING Junliang

CHENG Li

WANG Bohan

Related Institution

College of Energy and Power Engineering,Nanjing University of Aeronautics and Astronautics

Aeronautics Engineering College,Air Force Engineering University

Collaborative Innovation Center for Advanced Aero-Engines

南京航空航天大学能源与动力学院江苏省航空动力系统重点实验室

南京航空航天大学机械结构力学及控制国家重点实验室

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰