Failure mechanism of TiN/Ti strength and tough coating under high-speed sand-dust erosion

陈伟; 李舟; 赵振华; 颜诚; 马松林

doi:10.13224/j.cnki.jasp.2019.09.002

Chinese

您当前的位置：

首页 >

文章列表页 >

Failure mechanism of TiN/Ti strength and tough coating under high-speed sand-dust erosion

更新时间：2026-07-07

- Failure mechanism of TiN/Ti strength and tough coating under high-speed sand-dust erosion
- Vol. 34, Issue 9, Pages: 1866-1872(2019)
- 作者机构：
  
  南京航空航天大学能源与动力学院航空发动机热环境与热结构工业和信息化部重点实验室,南京,210016
- 作者简介：
- 基金信息：
- DOI：10.13224/j.cnki.jasp.2019.09.002
  CLC：
- Published：2019
- 稿件说明：
移动端阅览
陈伟, 李舟, 赵振华, 颜诚, 马松林. TiN/Ti强韧涂层在砂尘高速冲蚀下的失效机理[J]. 航空动力学报, 2019, 34(9): 1866-1872.

doi: 10.13224/j.cnki.jasp.2019.09.002
陈伟, 李舟, 赵振华, 颜诚, 马松林. TiN/Ti强韧涂层在砂尘高速冲蚀下的失效机理[J]. 航空动力学报, 2019, 34(9): 1866-1872. DOI： 10.13224/j.cnki.jasp.2019.09.002.

doi: 10.13224/j.cnki.jasp.2019.09.002 DOI：

摘要

利用高速连续冲蚀试验系统

在不同的冲击角及供砂量下

对有无TiN/Ti强韧涂层的不锈钢试件进行了砂尘高速冲蚀试验

获得了试件的质量冲蚀率。采用扫描电镜(SEM)对涂层损伤表面及断面形貌进行观测与分析

研究TiN/Ti涂层在不同冲击条件下的失效机理。结果表明：TiN/Ti涂层质量冲蚀率随冲击角及供砂量的增加而增加。在低冲击角下

砂尘粒子的切削作用是导致涂层材料剥落的主要原因；高冲击角下

砂尘冲击引起的裂纹萌生及扩展致使涂层材料块状破碎而剥落。TiN/Ti涂层显著提高了不锈钢的抗冲蚀性能

尤其是在低冲击角下。低冲击角下

涂层能将不锈钢的冲蚀性能提高约5倍；高冲击角下能提高约2倍。

Abstract

Through high-speed continuous erosion test system

high-speed sand-dust erosion tests of stainless steel specimens with or without TiN/Ti strength and tough coating were carried out at different impact angles and sand supplies

and the mass erosion rates of specimens were obtained. The surface and cross-sectional damage morphology of the coating were observed by scanning electron microscopy (SEM)

and the failure mechanism of TiN/Ti coatings under different impact conditions was analyzed. The results show that the mass erosion rate of TiN/Ti coatings increases with the increase of impact angle and sand supply. At low impact angle

the cutting action of sand particles is the main reason for the spalling of coatings; at high impact angle

the crack initiation and propagation caused by sand-dust impact lead to massive fragmentation and spalling of coatings. TiN/Ti coating can significantly improve the erosion resistance of stainless steel

especially at low impact angle.At low impact angle

the erosion resistance of stainless steel with coating can be increased by about 5 times

and at high impact angle it can be increased by about 2 times.

关键词

Keywords

references

Views

1017

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Bending fatigue failure mechanism of the new high temperature carburizing stainless aviation steel gear

Test of the weft mechanical properties of 2.5D woven composites

Thermal fatigue behavior of nickle based superalloy GH536

组合式弹性金属密封泄漏特性实验研究与结构优化

基于三维接触摩擦单元的套齿连接解析建模研究

Related Author

Xin TANG

Rupeng ZHU

Maosheng YANG

Peng TANG

Fajia LI

Xingbo XIONG

赵哲

温卫东

Related Institution

Science and Technology on Helicopter Transmission Laboratory，Nanjing University of Aeronautics and Astronautics

Science and Technology on Helicopter Transmission Laboratory，Hunan Aviation Powerplant Research Institute，Aero Engine Corporation of China

Institute of Special Steel，Central Iron and Steel Research Institute

School of Mechanical Engineering，University of Jinan

南京航空航天大学能源与动力学院江苏省航空动力系统重点实验室

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰