Experimental Study on Wear Resistance in Surface Modification Processof Cr12MoV via DLC Coating and Nitriding/QPQ

何霞; 庞国英; 钟林; 王国荣; 魏刚

doi:10.13433/j.cnki.1003-8728.20230115

Chinese

您当前的位置：

首页 >

文章列表页 >

Experimental Study on Wear Resistance in Surface Modification Processof Cr12MoV via DLC Coating and Nitriding/QPQ

更新时间：2026-07-10

- Experimental Study on Wear Resistance in Surface Modification Processof Cr12MoV via DLC Coating and Nitriding/QPQ
- Mechanical Science and Technology for Aerospace Engineering Vol. 43, Issue 12, Pages: 2168-2175(2024)
- 作者机构：
  
  1. 西南石油大学机构机电工程学院,成都,610500
  2. 西南石油大学能源装备研究院,成都,610500
- 作者简介：
- 基金信息：
- DOI：10.13433/j.cnki.1003-8728.20230115
  CLC：
- Published：2024
- 稿件说明：
移动端阅览
何霞, 庞国英, 钟林, et al. Experimental Study on Wear Resistance in Surface Modification Processof Cr12MoV via DLC Coating and Nitriding/QPQ[J]. Mechanical Science and Technology for Aerospace Engineering, 2024, 43(12): 2168-2175.
DOI：

何霞, 庞国英, 钟林, et al. Experimental Study on Wear Resistance in Surface Modification Processof Cr12MoV via DLC Coating and Nitriding/QPQ[J]. Mechanical Science and Technology for Aerospace Engineering, 2024, 43(12): 2168-2175. DOI： 10.13433/j.cnki.1003-8728.20230115.

摘要

为探究冷作模具钢Cr12MoV基底表面DLC涂层(Diamond-like carbon films)、渗氮和盐浴复合处理 (Quench-Polish-Quench，QPQ)表面改性工艺的耐磨性能优劣。基于摩擦试验机的高频往复球-盘配对副，在模拟测试工况下开展表面改性工艺的Cr12MoV试样盘与Si3N4陶瓷球配对的摩擦磨损性能实验。研究表明，在模拟测试工况下，综合摩擦因数和体积磨损率分析，DLC涂层工艺更适合改善Cr12MoV表面耐磨性能，其耐磨性能相比渗氮和QPQ提高了4倍以上，其Si3N4陶瓷对磨球表面形成碳质转移膜，阻止DLC材料的磨损。DLC试验盘粘着程度比渗氮试验盘严重，是由于高硬度比低硬度金属抗粘着能力强。DLC与QPQ试样盘表面发生塑性变形，且QPQ试样盘表面形成片状剥落坑。

Abstract

To explore the wear resistance in the surface modification processof DLC coating (Diamond like carbon films)

nitriding and salt bath composite treatment (Quench Polish Quench

QPQ) on the substrate surface of cold work die steel Cr12MoV. Based on the high-frequency reciprocating ball disk pairing pair of the friction testing machine

the friction and wear properties of the surface modified Cr12MoV sample disk paired with Si3N4 ceramic ball were tested under the simulated conditions. The study showed that under the simulated conditions

the analysis of friction coefficient and volume-wear rate showed that DLC coating was more suitable for improving the wear resistance of Cr12MoV surface

and its wear resistance is more than 4 times higher than that vianitriding/QPQ

a carbon transfer film is formed on the surface of Si3N4 ceramic grinding ball to prevent the wear of DLC material. DLC coating provides the experimental support for improving the wear resistance of Cr12MoV surface.The adhesion degree of DLC test plate is more serious than that of nitriding test plate

because the high hardness metal has stronger anti-adhesion ability than that of the low hardness metal. The surface of DLC and QPQ sample discs has plastic deformation

and the surface of QPQ sample disc formed flake pits.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on Joining Mechanism and Mechanical Properties of Friction Stir Riveting of CF/PEEK-AA7075 Sheets

Least-squares Support Vector Machine Prediction Modeling of MFC Piezoelectric Actuators Function Degradation

Research on Continuous Obstacle Avoidance Trajectory Planning and Tracking Control Strategies for Low Speed Intelligent Vehicles with Different Road Curvature Changes

Gait Design and Motion Analysis of Hexapod Bionic Robots

Improved RRT Algorithm for Obstacle Avoidance in Robotic Arm Path Planning

Related Author

No data

Related Institution

No data

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰