Effect of Rare Earth on Microstructure and Properties of Low Carbon Cast Steel Containing Ni

JIANG Yan-liang; GUO Hai-long; GUO Er-jun; FENG Yi-cheng

doi:10.15938/j.jhust.2016.06.023

Chinese

您当前的位置：

首页 >

文章列表页 >

Effect of Rare Earth on Microstructure and Properties of Low Carbon Cast Steel Containing Ni

更新时间：2026-08-31

- Effect of Rare Earth on Microstructure and Properties of Low Carbon Cast Steel Containing Ni
- Vol. 21, Issue 6, Pages: 123-126(2016)
- 作者机构：
  
  1. [1]中航工业哈尔滨东安发动机(集团)有限公司,黑龙江,哈尔滨,150066
  2. [2]哈尔滨理工大学材料科学与工程学院,黑龙江,哈尔滨,150040
- 作者简介：
- 基金信息：
- DOI：10.15938/j.jhust.2016.06.023
  CLC： TG142
- Published：2016
- 稿件说明：
移动端阅览
JIANG Yan-liang, GUO Hai-long, GUO Er-jun, et al. Effect of Rare Earth on Microstructure and Properties of Low Carbon Cast Steel Containing Ni[J]. 2016, 21(6): 123-126.
DOI：

JIANG Yan-liang, GUO Hai-long, GUO Er-jun, et al. Effect of Rare Earth on Microstructure and Properties of Low Carbon Cast Steel Containing Ni[J]. 2016, 21(6): 123-126. DOI： 10.15938/j.jhust.2016.06.023.

摘要

以含镍低碳铸钢为研究对象

通过改变一号稀土加入量

经过金相组织观察、拉伸试验、冲击试验、夹杂物形貌分析、能谱分析等

研究RE含量变化对铸钢试样组织和性能的影响.研究结果表明：铸钢试样经调质处理后

组织为细小回火索氏体

存在少量铁素体.随着一号稀土质量分数增加

回火索氏体含量增多

晶粒尺寸减小;长条状或者尖角状夹杂物减少

稀土夹杂物主要是以球状或者近球状的形态存在

大小在5～10μm.抗拉强度、屈服强度和布氏硬度总体上呈现不断增加的趋势

在一号稀土含量为0.5%时

其值最高

抗拉强度为905.2 MPa

屈服强度为776.7 MPa

布氏硬度为274.冲击功先增加后降低

一号稀土质量分数在0.3%时

冲击功值为80 J.

Abstract

The effect of RE content on microstructure and mechanical properties of low carbon cast steel containing Ni was studied by optical microscope observation

tensile testing

impact testing

inclusion morphology analysis and EDS.The experimental results show that there are many tempered sorbite and a little ferrite in quenching and tempering cast steel.The content of tempered sorbite increases and the size of tempered sorbite decreases with increasing of RE.Additive of RE improves the morphology of inclusion

the inclusion containing RE is sphere-like

and the size is 5 μm-10 μm.The strength and hardness increase with increasing of RE content

the maximum value of ultimate tensile strength

yield strength and hardness is 905.2 MPa

776.7 MPa and 274

respectively.The impact energy increases firstly and then decreases with increasing of RE content.The maximum value of impact energy is 80 J when the content of RE is 0.3%.

关键词

Keywords

references

Views

652

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Mn对Mg-Zn-Ca-Mn合金显微组织和力学性能的影响

The Effect of Ni Content on the Microstructure and Mechanical Properties of Heat Resistant Ductile Iron with Heavy Section

Mechanical Properties and Dielectric Properties of Bismaleimide Composites Modified by Multi-walled Carbon Nanotubes and Polyethersulfone

Micro-morphology and Properties of OMMT/PES/BMI Composites

The Influence of Sintering Temperature and Composition on Mechanical Properties of Al2O3-Ti C Composites

Related Author

PEI Teng

ZHUANG Yuan

YU Yan-dong

SUN Jun

WANG Liping

SHAO Shibo

YUAN Wei

FENG Yicheng

Related Institution

School of Materials Science and Engineering, Harbin University of Science and Technology

School of Material Science and Chemical Engineering, Harbin University of Science and Technology

School of Mechanical Engineering, Shandong University of Technology

Tianrun Industrial Technology Co. , Ltd.

Key Laboratory of Engineering Dielectrics and Its Application,Ministry of Education, Harbin University of Science and Technology

AI问答

Postal code：100079
Tel：（010）53879206 Email：tmw@bjxintong.com.cn
Technical support is provided by Beijing Founder electronics co., LTD 京ICP备09082226号-64 京公网安备11010602201714号
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰