- 高温、高应变率LY12铝压缩动态力学性能实验
- Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures
- 航空动力学报 2009年24卷第4期
- 作者机构：
  
  1. 中国工程物理研究院结构力学研究所,绵阳,621900
  2. 北京航空航天大学固体力学所,北京,100191
- 作者简介：
- 基金信息：
  
  国家自然科学基金(10572013)
- DOI：
  中图分类号：
- 纸质出版：2009
- 稿件说明：
移动端阅览
谢若泽, 张方举, 邓志方, 等. 高温、高应变率LY12铝压缩动态力学性能实验[J]. 航空动力学报, 2009,24(4).

XIE Ruo-ze, ZHANG Fang-ju, DENG Zhi-fang, et al. Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures[J]. 2009, 24(4).
谢若泽, 张方举, 邓志方, 等. 高温、高应变率LY12铝压缩动态力学性能实验[J]. 航空动力学报, 2009,24(4). DOI：

XIE Ruo-ze, ZHANG Fang-ju, DENG Zhi-fang, et al. Experimental investigation into dynamic compressive mechanical properties of LY12 at high strain rates and high temperatures[J]. 2009, 24(4). DOI：

摘要

利用配备自动组装系统和高温加热系统的直径为 ф5 mm的Hopkinson压杆

对温度在20℃～400℃、应变率在(5～14)×103s-1范围内LY12铝的动态压缩力学性能进行了实验研究.实验中采用波形整形技术

有效地消除了入射波的高频振荡

提高了测试精度.实验结果表明:当实验温度低于200℃时

温度的影响较小

而高于200℃时

材料的温度软化效应将十分明显

且随着温度的升高

流动应力逐步降低;LY12铝的性质接近于线性硬化材料

随温度的升高

其硬化模量逐步降低;在(5～14)×103s-1应变率范围内

LY12铝的动态压缩性能的应变率效应并不明显.

Abstract

The dynamic mechanical properties of LY12 aluminum were studied experimentally by Hopkinson Bar of diameter 5mm with an automatic assembling system and heating system

within the range of temperature from 20℃ to 400℃ and strain-rate from 5×103s-1 to 1.4×104s-1.In the experiments

a shaper was used to eliminate the oscillation of high frequency in the incident signal and to improve the experimental precision of bar system.The experimental results show that the effect of temperature on dynamic properties of LY12 is not great at temperature lower than 200℃;on the contrary

the thermal softening effect is obvious at temperature higher than 200℃

exhibiting the decrease of flow stresses and linear harden modulus with increase of temperature

which is similar to linear harden materials.From the experiments

the dynamic properties of LY12 don't show strong sensitivity to the strain rates.

关键词

Keywords

references

浏览量

437

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

高温环境下角接触球轴承磨损寿命分析

三维四向C/C复合材料高温氧化环境强度预测

4种典型航空钛合金材料高温裂纹扩展性能对比试验

瞬态热冲击环境下金属蜂窝板结构的热防护特性

石墨密封材料高温摩擦磨损行为及预测