静电纺丝制备EVOH-S03Li/Si0:无纺布 形貌及热特性研究

巩桂芬; 王力; 李晓东; 兰健

Chinese

您当前的位置：

首页 >

文章列表页 >

静电纺丝制备EVOH-S03Li/Si0:无纺布形貌及热特性研究

材料科学与工程 | 更新时间：2026-08-31

- 静电纺丝制备EVOH-S03Li/Si0:无纺布形貌及热特性研究
- Investigation on Microcosmic Morphology and Thermal Properties of Electro一saun EVOH一SO} Li/SiO} Non一woven Membrane
- 哈尔滨理工大学学报 2015年20卷第2期页码：101-104
- 作者机构：
  
  哈尔滨理工大学材料科学与工程学院,黑龙江,哈尔滨,150040
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TQ340.649
- 纸质出版：2015
- 稿件说明：
移动端阅览
巩桂芬, 王力, 李晓东, 等. 静电纺丝制备EVOH-S03Li/Si0:无纺布形貌及热特性研究[J]. 哈尔滨理工大学学报, 2015,20(2):101-104.

GONG Gui-feu, WANG Li LI Xiao-dour, LAN Jiau. Investigation on Microcosmic Morphology and Thermal Properties of Electro一saun EVOH一SO} Li/SiO} Non一woven Membrane[J]. 2015, 20(2): 101-104.
巩桂芬, 王力, 李晓东, 等. 静电纺丝制备EVOH-S03Li/Si0:无纺布形貌及热特性研究[J]. 哈尔滨理工大学学报, 2015,20(2):101-104. DOI：

GONG Gui-feu, WANG Li LI Xiao-dour, LAN Jiau. Investigation on Microcosmic Morphology and Thermal Properties of Electro一saun EVOH一SO} Li/SiO} Non一woven Membrane[J]. 2015, 20(2): 101-104. DOI：

摘要

为研究掺杂纳米SiOZ对EVOH磺酸铿( EVOH-S03 Li)无纺布形貌及热特性影响，以聚乙烯一乙烯醇(EVOH)和1

3一丙烷磺酸内醋为原料，叔丁醇铿为催化剂，合成EVOH磺酸铿接枝聚合物，并进行纳米SiOZ掺杂改性，经静电纺丝制备出EVOH-S03Li

EVOH一S03 Li/SiOZ两种无纺布;应用扫描电镜观察分析了无纺布的微观形貌，并通过差示扫描量热仪及热失重仪对无纺布热性能进行研究分析;结果表明:经纳米SiOZ改性后，纤维直径降低，分布在0. 1 } 0. 2 N.

m之间，无纺布结晶度升高，熔点提高35 0C，起始热分解温度升高30 0C .

Abstract

To study the influence of SiOznn macrocosmicmorphology and thermal properties of EVOH一S03 Linon-woven，with Lithium Tert-butoxide asthe catalystend-capped with lithium sulfonate(EVOH一S03Li)a polymer electrolyte of poly(ethylene-co-vinyl alcohol)synthesized from poly(ethylene-co-vinyl alcohol) and were added into EVOH-S03Li solution and the EVOH一S03 Li，EVOH一S03 Li/SiOz non-woven membraneswere prepared by electro一spinning technique. Scanning Electron MicrosG’Ope W9sutilized to characterize the features microcosmic of the non-woven，meanwhile，Differential Scanning Cal-orimetry and Thermal gravimetric analyzer wereused to characterize thermal properties of the non-woven. Thecults showed that，with the addition of SiOz，the fiber diameter of non-woven membraneW9

s slen(ler

It W9

stween 0. 1-0. 2 Nm，moreover，the degree of crystallinity became higher and melting point increased by 35℃，ther-mal decomposition temperature increased by 30℃.

关键词

Keywords

references

浏览量

833

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

EVOH 磺酸锂电池隔膜的制备及微观形貌

WTConv-Informer 结合频率增强通道注意力的温度预测方法

不同温度环氧纳米复合材料击穿机制

基于区块链的电力系统最优潮流分布式求解算法

融合局部与全局特征的轻量化乳腺肿瘤分类模型