On Equilibrium Ga Intergranular Films in Cr2GaC

Original Reports | 更新时间：2026-08-19

- On Equilibrium Ga Intergranular Films in Cr2GaC
- On Equilibrium Ga Intergranular Films in Cr2GaC
- 材料研究快报（英文） 2013年1卷第2期页码：109-113
- 作者机构：
  
  1. National Institute of Advanced Industrial Science and Technology (AIST) Nagoya
  2. Department of Materials Science and Engineering Drexel University Philadelphia PA
  3. Department of Materials Science and Engineering Southeast University
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2013.794374
  中图分类号：
- 网络首发：2013-04-24，
  
  纸质出版：2013
- 稿件说明：
移动端阅览
ZhengMing Sun, Michel W. Barsoum, Yamei Zhang, 等. On Equilibrium Ga Intergranular Films in Cr2GaC[J]. 材料研究快报（英文）, 2013,1(2):109-113.

ZhengMing Sun, Michel W. Barsoum, Yamei Zhang, et al. On Equilibrium Ga Intergranular Films in Cr2GaC[J]. Materials Research Letters, 2013, 1(2): 109-113.
ZhengMing Sun, Michel W. Barsoum, Yamei Zhang, 等. On Equilibrium Ga Intergranular Films in Cr2GaC[J]. 材料研究快报（英文）, 2013,1(2):109-113. DOI： 10.1080/21663831.2013.794374.

ZhengMing Sun, Michel W. Barsoum, Yamei Zhang, et al. On Equilibrium Ga Intergranular Films in Cr2GaC[J]. Materials Research Letters, 2013, 1(2): 109-113. DOI： 10.1080/21663831.2013.794374.

摘要

The presence of equilibrium intergranular films (IGFs) in metallic systems has long been postulated; compelling evidence for this idea

however

is still lacking. Herein differential scanning calorimetry

in the−60°C to 70°C temperature range

on bulk and Cr

GaC powders was carried out. A sharp endothermic trough

roughly 50°C below the melting point of bulk pure Ga

in the powdered samples was taken to be strong evidence for the presence of IGFs in the latter. The troughs for the sintered body were much more diffuse suggesting that in this case

a distribution of grain boundary thicknesses exists. A temperature dependent adsorption energy is postulated to explain the reversible extrusion and resorption of 100 μm thick Ga micro-pillars.

Abstract

The presence of equilibrium intergranular films (IGFs) in metallic systems has long been postulated; compelling evidence for this idea

however

is still lacking. Herein differential scanning calorimetry

in the−60°C to 70°C temperature range

on bulk and Cr

GaC powders was carried out. A sharp endothermic trough

roughly 50°C below the melting point of bulk pure Ga

in the powdered samples was taken to be strong evidence for the presence of IGFs in the latter. The troughs for the sintered body were much more diffuse suggesting that in this case

a distribution of grain boundary thicknesses exists. A temperature dependent adsorption energy is postulated to explain the reversible extrusion and resorption of 100 μm thick Ga micro-pillars.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

High-cycle fatigue behavior in heterostructured materials: a perspective

Combined first-principles calculation and machine learning for the strength of segregated grain boundaries in aluminum

Correlative 3D imaging of internal damage accumulation and 2D surface strain mapping during tensile straining

Dual effect of oxide inclusions in additively manufactured nickel superalloys

Thermo-mechanical-coupling-induced structural transformation and strain-hardening in Ti-V-Zr-Nb-Al multi-component alloys