Cracking in a Fe–25Mn–3Si–3Al Steel

Xiaoyang Fang; Lihui Zhang; Wei Liu; Kangying Shu; Youtong Fang; Yuewu Zeng; Liang Meng; Jiabin Liu

doi:10.1080/21663831.2014.915433

Chinese

您当前的位置：

首页 >

文章列表页 >

Cracking in a Fe–25Mn–3Si–3Al Steel

Original Reports | 更新时间：2026-08-19

- Cracking in a Fe–25Mn–3Si–3Al Steel
- Cracking in a Fe–25Mn–3Si–3Al Steel
- 材料研究快报（英文） 2014年2卷第4期页码：204-208
- 作者机构：
  
  1. Department of Materials Science and Engineering Zhejiang University
  2. Department of Materials Science and Engineering China Jiliang University
  3. Department of Materials Science and Engineering Zhejiang University Hangzhou People's Republic of China,310027
  4. College of Electrical Engineering Zhejiang University
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2014.915433
  中图分类号：
- 网络首发：2014-05-08，
  
  纸质出版：2014
- 稿件说明：
移动端阅览
Xiaoyang Fang, Lihui Zhang, Wei Liu, 等. Cracking in a Fe–25Mn–3Si–3Al Steel[J]. 材料研究快报（英文）, 2014,2(4):204-208.

Xiaoyang Fang, Lihui Zhang, Wei Liu, et al. Cracking in a Fe–25Mn–3Si–3Al Steel[J]. Materials Research Letters, 2014, 2(4): 204-208.
Xiaoyang Fang, Lihui Zhang, Wei Liu, 等. Cracking in a Fe–25Mn–3Si–3Al Steel[J]. 材料研究快报（英文）, 2014,2(4):204-208. DOI： 10.1080/21663831.2014.915433.

Xiaoyang Fang, Lihui Zhang, Wei Liu, et al. Cracking in a Fe–25Mn–3Si–3Al Steel[J]. Materials Research Letters, 2014, 2(4): 204-208. DOI： 10.1080/21663831.2014.915433.

摘要

Abstract

Fe–25Mn–3Si–3Al steels obtained much attention because of their excellent mechanical properties. However

the fracture behavior of the steels remains unclear. In this study

Fe–25Mn–3Si–3Al steels were

ex situ

tensile strained and tested by a transmission electron microscope to investigate the relationship between crack and twins. The propagation of crack was examined and related to the dislocation slip and twinning. Cracks initiate related to the moving of dislocations and propagate along the slip bands. Twins parallel and inclined to the crack are produced during crack propagating. The inclined twins notably block and blunt the crack

whereas the parallel twins exhibit an insignificant effect.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Imaging the deformation-induced accumulation of defects in nanoporous gold

On the strain rate-dependent deformation mechanism of CoCrFeMnNi high-entropy alloy at liquid nitrogen temperature

Microstructural specificity of optimal creep performance in Ni-based single crystal superalloys under 980°C-250 MPa and 1100°C-137 MPa conditions

Bi addition increases strength and strain-softening behavior in SAC305

Origin of radiation damage variability in different phases of Al-Cr-Fe-Ni-V high-entropy alloy with heterogeneous microstructures

相关机构

Institute of Materials Physics and Technology Hamburg University of Technology

Department of Materials Science and Engineering Pohang University of Science and Technology

Department of Materials Science and Engineering Chungnam National University

Department of Materials Science and Engineering Pohang University of Science and Technology Pohang Republic of Korea

Center for High Entropy Alloys Pohang University of Science and Technology

AI问答

地址：北京市丰台区顺八条1号院2号楼北阳晨光大厦2层邮编：100079
联系电话：（010）53879206 Email：tmw@bjxintong.com.cn
技术支持由北京北大方正电子有限公司提供京ICP备09082226号-64 京公网安备11010602201714号
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰