Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates

Josef Cobb; Shraddha Vachhani; Robert M. Dickerson; Patricia O. Dickerson; Weizhong Han; Nathan A. Mara; John S. Carpenter; Judy Schneider

doi:10.1080/21663831.2014.918567

Chinese

您当前的位置：

首页 >

文章列表页 >

Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates

Original Reports | 更新时间：2026-08-19

- Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates
- Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates
- 材料研究快报（英文） 2014年2卷第4期页码：227-232
- 作者机构：
  
  1. Mechanical Engineering Department Mississippi State University Starkville
  2. Mechanical Engineering Department Georgia Institute of Technology Atlanta
  3. Materials Science and Technology Division Los Alamos National Laboratory Los Alamos
  4. Center for Advancing Materials Performance from the Nanoscale State Key Laboratory for Mechanical Behavior of Materials Xi'an Jiaotong University Xi'an People's Republic of China,710049
  5. Materials Science and Technology Division Los Alamos National Laboratory Los Alamos 45 USA,NM875
  6. Center for Integrated Nanotechnologies Los Alamos National Laboratory Los Alamos
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2014.918567
  中图分类号：
- 网络首发：2014-05-22，
  
  纸质出版：2014
- 稿件说明：
移动端阅览
Josef Cobb, Shraddha Vachhani, Robert M. Dickerson, 等. Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates[J]. 材料研究快报（英文）, 2014,2(4):227-232.

Josef Cobb, Shraddha Vachhani, Robert M. Dickerson, et al. Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates[J]. Materials Research Letters, 2014, 2(4): 227-232.
Josef Cobb, Shraddha Vachhani, Robert M. Dickerson, 等. Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates[J]. 材料研究快报（英文）, 2014,2(4):227-232. DOI： 10.1080/21663831.2014.918567.

Josef Cobb, Shraddha Vachhani, Robert M. Dickerson, et al. Layer Stability and Material Properties of Friction-Stir Welded Cu–Nb Nanolamellar Composite Plates[J]. Materials Research Letters, 2014, 2(4): 227-232. DOI： 10.1080/21663831.2014.918567.

摘要

Initial efforts to friction-stir weld (FSW) Cu–Nb nanolamellar composite plates fabricated via accumulative roll bonding are reported in this study. Parent material layers within the composite were nominally 300 nm and exhibited a hardness of 2.5 GPa. After FSW

two types of microstructures were present: a refined layered structure

and an equiaxed nanocrystalline microstructure with grain diameters on the order of 7 nm. The type of microstructure was dependent on location within the FSW nugget and related to varying amounts of strain. Material hardness increased with refinement

with the equiaxed microstructure reaching a maximum hardness of 6.0 GPa.

Abstract

two types of microstructures were present: a refined layered structure

with the equiaxed microstructure reaching a maximum hardness of 6.0 GPa.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Microstructural specificity of optimal creep performance in Ni-based single crystal superalloys under 980°C-250 MPa and 1100°C-137 MPa conditions

Dislocation mechanism of the Re-W synergistic strengthening effect in nickel-based single crystal model superalloy

Combined first-principles calculation and machine learning for the strength of segregated grain boundaries in aluminum

Thermo-mechanical-coupling-induced structural transformation and strain-hardening in Ti-V-Zr-Nb-Al multi-component alloys

Dual effect of oxide inclusions in additively manufactured nickel superalloys