Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy

I. S. Wani; T. Bhattacharjee; S. Sheikh; Y. P. Lu; S. Chatterjee; P. P. Bhattacharjee; S. Guo; N. Tsuji

doi:10.1080/21663831.2016.1160451

Chinese

您当前的位置：

首页 >

文章列表页 >

Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy

Original Reports | 更新时间：2026-08-19

- Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy
- Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy
- 材料研究快报（英文） 2016年4卷第3期页码：174-179
- 作者机构：
  
  1. Department of Materials Science and Metallurgical Engineering IIT Hyderabad Kandi 5,502 28
  2. Department of Materials Science and Engineering Kyoto University Yoshida Honmachi Sakyo,ku
  3. Department of Materials and Manufacturing Technology Chalmers University of Technology
  4. Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province) School of Materials Science and Engineering Dalian University of Technology
  5. Department of Materials Science and Engineering Kyoto University Yoshida Honmachi Sakyo-ku Kyoto Japan,606-8501
  6. Elements Strategy Initiative for Structural Materials (ESISM)
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2016.1160451
  中图分类号：
- 网络首发：2016-03-25，
  
  纸质出版：2016
- 稿件说明：
移动端阅览
I. S. Wani, T. Bhattacharjee, S. Sheikh, 等. Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy[J]. 材料研究快报（英文）, 2016,4(3):174-179.

I. S. Wani, T. Bhattacharjee, S. Sheikh, et al. Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy[J]. Materials Research Letters, 2016, 4(3): 174-179.
I. S. Wani, T. Bhattacharjee, S. Sheikh, 等. Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy[J]. 材料研究快报（英文）, 2016,4(3):174-179. DOI： 10.1080/21663831.2016.1160451.

I. S. Wani, T. Bhattacharjee, S. Sheikh, et al. Ultrafine-Grained AlCoCrFeNi2.1 Eutectic High-Entropy Alloy[J]. Materials Research Letters, 2016, 4(3): 174-179. DOI： 10.1080/21663831.2016.1160451.

摘要

Abstract

The development of microstructure and mechanical properties was investigated in a heavily cold-rolled and annealed AlCoCrFeNi

2.1

high-entropy alloy. The as-cast alloy having a eutectic morphology consisting of alternate bands of ordered L1

and B2 phases was 90% cold-rolled. The deformed microstructure showed profuse shear banding and disordering of the L1

but no transformation of the B2 phase. A duplex microstructure consisting of ultrafine equiaxed grains (∼0.60 µm) of disordered face centered cubic and B2 was observed after annealing at 800°C. The annealed material showed remarkable strength–ductility combination having ultimate tensile strength ∼1.2 GPa and elongation to failure ∼12%.

Impact Statement:

AlCoCrFeNi

2.1

eutectic HEA with ordered L1

and B2 phases can be thermo-mechanically processed to achieve ultrafine structure and remarkable strength-ductility properties.

关键词

Keywords

references

浏览量

下载量

439

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Microstructures and properties of high-entropy alloy films and coatings: a review

Cryogenic nano-twinning engineering to mitigate the strength–hydrogen embrittlement trade-off in a high-entropy alloy

Deciphering the exceptional chemical activity of a High-entropy metallic glass

CMT wire arc additive manufactured ultra-high strength WE43 alloy via in-situ cooling and precipitation regulating

Multistep severe plastic deformation to achieve non-rare earth bulk magnets with high α-MnBi phase content

相关机构

Department of Materials Science and Engineering The University of Tennessee Knoxville

School of Materials Science and Engineering University of Shanghai for Science and Technology

Advanced Institute for Materials Research (WPI-AIMR) Tohoku University

Center for Heterogenic Metal Additive Manufacturing Pohang University of Science and Technology (POSTECH) Pohang Republic of Korea

Department of Materials Science and Engineering Pohang University of Science and Technology (POSTECH) Pohang Republic of Korea

AI问答

地址：北京市丰台区顺八条1号院2号楼北阳晨光大厦2层邮编：100079
联系电话：（010）53879206 Email：tmw@bjxintong.com.cn
技术支持由北京北大方正电子有限公司提供京ICP备09082226号-64 京公网安备11010602201714号
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰