Low temperature structural stability of Fe90Sc10 nanoglasses

Original Reports | 更新时间：2026-08-19

- Low temperature structural stability of Fe90Sc10 nanoglasses
- Low temperature structural stability of Fe90Sc10 nanoglasses
- 材料研究快报（英文） 2018年6卷第3期页码：178-183
- 作者机构：
  
  1. TUD Joint Research Laboratory Nanomaterials Technische Universität Darmstadt,KIT
  2. Karlsruhe Nano Micro Facility Karlsruhe Institute of Technology
  3. Karlsruhe Nano Micro Facility Karlsruhe Institute of Technology Eggenstein-Leopoldshafen Germany
  4. Helmholtz Institute Ulm Karlsruhe Institute of Technology
  5. Institute of Nanotechnology Karlsruhe Institute of Technology
  6. Institute of Nanotechnology Karlsruhe Institute of Technology Eggenstein-Leopoldshafen Germany
  7. TUD Joint Research Laboratory Nanomaterials Technische Universität Darmstadt Darmstadt Germany,KIT
  8. Herbert Gleiter Institute of Nanoscience Nanjing University of Science and Technology
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2018.1430622
  中图分类号：
- 网络首发：2018-02-06，
  
  纸质出版：2018
- 稿件说明：
移动端阅览
Chaomin Wang, Tao Feng, Di Wang, 等. Low temperature structural stability of Fe90Sc10 nanoglasses[J]. 材料研究快报（英文）, 2018,6(3):178-183.

Chaomin Wang, Tao Feng, Di Wang, et al. Low temperature structural stability of Fe90Sc10 nanoglasses[J]. Materials Research Letters, 2018, 6(3): 178-183.
Chaomin Wang, Tao Feng, Di Wang, 等. Low temperature structural stability of Fe90Sc10 nanoglasses[J]. 材料研究快报（英文）, 2018,6(3):178-183. DOI： 10.1080/21663831.2018.1430622.

Chaomin Wang, Tao Feng, Di Wang, et al. Low temperature structural stability of Fe90Sc10 nanoglasses[J]. Materials Research Letters, 2018, 6(3): 178-183. DOI： 10.1080/21663831.2018.1430622.

摘要

Abstract

BSTRACTThe structural stability of Fe

nanoglasses has been studied by means of low temperature crystallization. Specimens were annealed

in situ

in a transmission electron microscope

and

ex situ

in an ultra-high vacuum tube-furnace. Both studies led to similar results. The structure of the Fe

nanoglasses was stable for up to 2 h when annealed at 150°C. Annealing the Fe

nanoglasses at higher temperature resulted in the formation of the nanocrystalline bcc-Fe(Sc).

Impact statement

The structural evolution of Fe

nanoglasses has been studied in detail during low temperature annealing. Our results indicate that the nanostructure of Fe

nanoglasses is quite stable at low temperature.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Imaging the in-plane distribution of helium precipitates at a Cu/V interface

Strength and plasticity of nanolaminated materials

Formation Mechanisms of High-density Growth Twins in Aluminum with High Stacking-Fault Energy

The Suppression of Instabilities via Biphase Interfaces During Bulk Fabrication of Nanograined Zr

Twinnability of bimetal interfaces in nanostructured composites

相关机构

Department of Materials Science and Engineering Texas A&M University College Station

Department of Materials Science and Engineering Massachusetts Institute of Technology Cambridge

Center for Integrated Nanotechnologies Materials Phycicsand Applications Division Los Alamos National Laboratory Los Alamos

Materials Science and Technology Division Los Alamos National Laboratory Los Alamos

Department of Materials Science and Engineering University of Michigan Ann Arbor

AI问答

地址：北京市丰台区顺八条1号院2号楼北阳晨光大厦2层邮编：100079
联系电话：（010）53879206 Email：tmw@bjxintong.com.cn
技术支持由北京北大方正电子有限公司提供京ICP备09082226号-64 京公网安备11010602201714号
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰