Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation

Ying Zhong; Chunqing Wang; Jin Wang; Huiwen Ma; Sriram Krishnamoorthy; Vladislav Paley; Zijian Weng; Sungho Jin

doi:10.1080/21663831.2020.1791272

Chinese

您当前的位置：

首页 >

文章列表页 >

Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation

Original Reports | 更新时间：2026-08-19

- Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation
- Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation
- 材料研究快报（英文） 2020年8卷第11期页码：431-437
- 作者机构：
  
  1. a Department of Mechanical Engineering University of South Florida Tampa FL USA
  2. b State Key Laboratory of Advanced Welding and Joining Harbin Institute of Technology Harbin People’s Republic of China
  3. b State Key Laboratory of Advanced Welding and Joining Harbin Institute of Technology
  4. a Department of Mechanical Engineering University of South Florida Tampa
  5. c Department of Mechanical and Aerospace Engineering University of California at San Diego La Jolla
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2020.1791272
  中图分类号：
- 网络首发：2020-07-10，
  
  纸质出版：2020
- 稿件说明：
移动端阅览
Ying Zhong, Chunqing Wang, Jin Wang, 等. Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation[J]. 材料研究快报（英文）, 2020,8(11):431-437.

Ying Zhong, Chunqing Wang, Jin Wang, et al. Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation[J]. Materials Research Letters, 2020, 8(11): 431-437.
Ying Zhong, Chunqing Wang, Jin Wang, 等. Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation[J]. 材料研究快报（英文）, 2020,8(11):431-437. DOI： 10.1080/21663831.2020.1791272.

Ying Zhong, Chunqing Wang, Jin Wang, et al. Spontaneous formation of sub-4 nm nanocrystalline alloy via polymorphic phase transformation[J]. Materials Research Letters, 2020, 8(11): 431-437. DOI： 10.1080/21663831.2020.1791272.

摘要

Abstract

new phase-transformation-induced path to spontaneous formation of extreme nanograin structure is reported.

In-situ-heating-mode-

microscopy exhibited a substantial grain-growth of Cu

. During cooling

the grain-growth continued

but it spontaneously switched to grain-refinement mode on phase transformation through ∼180 °C from

-Cu

η’

-Cu

ending up with an extremely small nanograin size of ∼2.5 nm. The cooling cycling always restores the nanograin size regardless of thermal exposure history

making this to be the first demonstration to

stabilize

the nanograin with its own spontaneous behavior. The Young’s Modulus was significantly reduced by ∼×3

and the elongation was remarkably increased by ∼×8 to ∼9%.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

New transformation mechanism of TiB from Bf to B27 structure in β-solidified TiAl alloys

Dislocation-mediated reversible grain rotation

Decoding deformation-induced phase transformation in a high entropy alloy via nanoindentation pop-in phenomenon

Simultaneously improving strength and ductility of laser-powder-bed-fused Al–Zn–Mg–Cu–Ti alloys by controlling phase structure of Al3Ti

Achieving uniform and wide phase transformation hysteresis in twin-wire arc additive manufactured NiTiNb alloy

相关机构

a State Key Laboratory of Solidification Processing Northwestern Polytechnical University

a State Key Laboratory of Solidification Processing Northwestern Polytechnical University Xi'an People’s Republic of China

b Chongqing Innovation Center Northwestern Polytechnical University

c Shaanxi Key Laboratory of Electrical Materials and Infiltration Technology School of Materials Science and Engineering Xi'an University of Technology

a Key Laboratory of Multifunctional Nanomaterials and Smart Systems Division of Advanced Materials Suzhou Institute of Nano-Tech and Nano-Bionics Chinese Academy of Sciences Suzhou People’s Republic of China

AI问答

地址：北京市丰台区顺八条1号院2号楼北阳晨光大厦2层邮编：100079
联系电话：（010）53879206 Email：tmw@bjxintong.com.cn
技术支持由北京北大方正电子有限公司提供京ICP备09082226号-64 京公网安备11010602201714号
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰