Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing

S. L. Xie; S. V. Divinski; Y. B. Lei; Z. B. Wang

doi:10.1080/21663831.2020.1827072

Chinese

您当前的位置：

首页 >

文章列表页 >

Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing

Original Reports | 更新时间：2026-08-19

- Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing
- Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing
- 材料研究快报（英文） 2021年9卷第2期页码：84-90
- 作者机构：
  
  1. a Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences Shenyang People’s Republic of China
  2. b School of Materials Science and Engineering University of Science and Technology of China
  3. c Institute of Materials Physics University of Münster
  4. a Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2020.1827072
  中图分类号：
- 网络首发：2020-11-24，
  
  纸质出版：2021
- 稿件说明：
移动端阅览
S. L. Xie, S. V. Divinski, Y. B. Lei, 等. Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing[J]. 材料研究快报（英文）, 2021,9(2):84-90.

S. L. Xie, S. V. Divinski, Y. B. Lei, et al. Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing[J]. Materials Research Letters, 2021, 9(2): 84-90.
S. L. Xie, S. V. Divinski, Y. B. Lei, 等. Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing[J]. 材料研究快报（英文）, 2021,9(2):84-90. DOI： 10.1080/21663831.2020.1827072.

S. L. Xie, S. V. Divinski, Y. B. Lei, et al. Accelerated grain boundary migration in nanolaminated interstitial-free steel during chromizing[J]. Materials Research Letters, 2021, 9(2): 84-90. DOI： 10.1080/21663831.2020.1827072.

摘要

Abstract

nanolaminated surface layer was produced on interstitial-free steel by surface mechanical rolling treatment. While the microstructure showed relatively high thermal stability during annealing at 500°C

significant grain boundary (GB) migration occurred in the nanolaminated surface layer during chromizing at the same temperature. GB diffusion of Cr was observed under the Harrison B-type regime in the chromized surface layer. The accelerated GB migration was discussed to be influenced by enhanced GB energy and mobility due to the GB diffusion and enrichment of Cr in nanolaminated structures. Meanwhile

the high stresses introduced during sample preparations also enhance the coarsening kinetics.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Enhanced hot-hardness in nanograined Nb with stable grain boundary at small grain size

Composition-dependent cluster-to-precipitate transformation in novel high-strength and heat-resistant Al–Zn–Mg–Cu alloys

Achieving superior high-temperature strength in nanostructured Al-Cu-Mn alloy with Sc addition

Ordered-serrated phase boundaries stabilize eutectic high-entropy alloys at high temperature

Enhanced age-hardening in a lean Mg-Al-Ca-Mn alloy by trace silver addition

相关机构

b State Key Laboratory of High Performance Roll Materials and Composite Forming School of Material Science and Engineering Hebei University of Technology Tianjin People’s Republic of China

a State Key Laboratory of Metastable Materials Science and Technology & School of Materials Science and Engineering Yanshan University Qinhuangdao People’s Republic of China

e Institute of Applied Physics of the National Academy of Sciences of Belarus

d Jiangsu Rongtai Industrial Co. Ltd.

c Key Laboratory of Automobile Materials of Ministry of Education School of Materials Science and Engineering Nanling Campus Jilin University

AI问答