Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system

Report | 更新时间：2026-08-19

- Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system
- Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system
- 材料研究快报（英文） 2023年11卷第9期页码：764-771
- 作者机构：
  
  1. a Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences Shenyang People’s Republic of China
  2. b School of Materials Science and Engineering University of Science and Technology of China
  3. a Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences
- 作者简介：
- 基金信息：
- DOI：10.1080/21663831.2023.2233993
  中图分类号：
- 网络首发：2023-07-12，
  
  纸质出版：2023
- 稿件说明：
移动端阅览
Yiming Zhong, Bo Zhang, Ling Fang, 等. Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system[J]. 材料研究快报（英文）, 2023,11(9):764-771.

Yiming Zhong, Bo Zhang, Ling Fang, et al. Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system[J]. Materials Research Letters, 2023, 11(9): 764-771.
Yiming Zhong, Bo Zhang, Ling Fang, 等. Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system[J]. 材料研究快报（英文）, 2023,11(9):764-771. DOI： 10.1080/21663831.2023.2233993.

Yiming Zhong, Bo Zhang, Ling Fang, et al. Giant hardening and formation of nanograined supersaturated solid solution in Al–Zn system[J]. Materials Research Letters, 2023, 11(9): 764-771. DOI： 10.1080/21663831.2023.2233993.

摘要

Abstract

Grain refinement via severe plastic deformation (SPD) can induce the decomposition of Al–Zn supersaturated solid solution

resulting in strain softening rather than hardening. So far

it is very challenging to improve the strength of binary Al–Zn alloy by refining grains through SPD. Herein

a single-phase supersaturated solid solution nanostructure with relaxed grain boundaries has been successfully generated in Al–21.7 at% Zn alloy by cryogenic high-pressure torsion. Instead of softening

giant hardening is achieved. The nanocrystalline Al–Zn alloy with grain size of 15 nm has an ultrahigh yield strength of about 642 MPa.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Development of novel lightweight and cost-effective Mg–Ce–Al wrought alloy with high strength

Correlative 3D imaging of internal damage accumulation and 2D surface strain mapping during tensile straining

Anomalous twinning in body-centered cubic metals

High-cycle fatigue behavior in heterostructured materials: a perspective

Bimodal α precipitation mediates deformation coordination and strength-ductility synergy in a Zr-rich metastable β Ti alloy