α-Fe2O3(001)及其掺杂表面吸附As2O3机制的密度泛函理论

更新时间：2026-10-22

- α-Fe2O3(001)及其掺杂表面吸附As2O3机制的密度泛函理论
- Density functional theory of the adsorption mechanism of As2O3 on α-Fe2O3(001) and its doped surface
- 哈尔滨工业大学学报 2022年54卷第7期页码：20-28
- 作者机构：
  
  1. 山东大学能源与动力工程学院, 高效节能及储能技术与装备山东省工程实验室,济南,250061
  2. Shandong Engineering Laboratory for High-efficiency Energy Conservation and Energy Storage Technology & Equipment, School of Energy and Power Engineering, Shandong University,Jinan,China,250061
  3. 佐治亚理工学院布鲁克贝尔可持续发展学院,佐治亚,亚特兰大,30332
  4. Brook Byers Institute for Sustainable Systems and School of Civil and Environmental Engineering, Georgia Institute of Technology,GA,Atlanta,United States,30332
  5. 齐鲁工业大学(山东省科学院) 新材料研究所,济南,250014
- 作者简介：
- 基金信息：
  
  山东省重大科技创新工程(2019JZZY020305);齐鲁工业大学(山东省科学院)科教产融合创新试点工程(2020KJC-ZD12)
- DOI：10.11918/202109143
  中图分类号： TQ534
- 纸质出版：2022
- 稿件说明：
移动端阅览
刘思彤, 牛胜利, 韩奎华, 等. α-Fe2O3(001)及其掺杂表面吸附As2O3机制的密度泛函理论[J]. 哈尔滨工业大学学报, 2022,54(7):20-28.

LIU Sitong, NIU Shengli, HAN Kuihua, et al. Density functional theory of the adsorption mechanism of As2O3 on α-Fe2O3(001) and its doped surface[J]. 2022, 54(7): 20-28.
刘思彤, 牛胜利, 韩奎华, 等. α-Fe2O3(001)及其掺杂表面吸附As2O3机制的密度泛函理论[J]. 哈尔滨工业大学学报, 2022,54(7):20-28. DOI： 10.11918/202109143.

LIU Sitong, NIU Shengli, HAN Kuihua, et al. Density functional theory of the adsorption mechanism of As2O3 on α-Fe2O3(001) and its doped surface[J]. 2022, 54(7): 20-28. DOI： 10.11918/202109143.

摘要

为提高催化剂抗砷能力

采用密度泛函理论（DFT）方法研究As2O3在α-Fe2O3(001)表面的吸附行为以及掺杂Mo、Mn、Ni对α-Fe2O3(001)表面As2O3吸附行为的影响。建立As2O3在α-Fe2O3(001)表面吸附模型和Mo、Mn、Ni掺杂的吸附模型

计算As2O3在催化剂表面的吸附能

分析成键态密度以及掺杂前后的As2O3在α-Fe2O3(001)表面的电荷布局。结果表明:这4种体系均发生电子转移

Mo掺杂活化了As2O3分子

使得As2O3倾向于吸附在Mo活性位点上

保护了Fe活性位点

增强α-Fe2O3抗砷中毒能力；Mn、Ni掺杂后As2O3反应活性低于掺杂前

抑制了As与掺杂剂的吸附

导致Fe位点更易中毒

不利于之后的NH3-SCR反应。

Abstract

In this paper

density functional theory (DFT) method is used to study the adsorption behavior of As2O3 on α-Fe2O3(001) surface and the influence of doping Mo

Mn and Ni on the adsorption behavior of As2O3 on α-Fe2O3(001) surface. The adsorption model of As2O3 on the surface of α-Fe2O3(001) and the adsorption model of Mo

Mn and Ni doping were established. The adsorption energy of As2O3 on the catalyst surface was calculated. The density of bonding states and the charge layout of As2O3 on the surface of α-Fe2O3(001) before and after doping are analyzed. Electron transfer occurs in the four systems. Mo doping activates As2O3 molecules

makes As2O3 tend to be adsorbed on Mo active sites

protects Fe active sites

and enhances the anti-arsenic poisoning ability of α-Fe2O3. After Mn and Ni doping

the reaction activity of As2O3 is lower than before

which inhibits the adsorption of As2O3 and increases the poisoning effect of the catalyst

which is not conducive to the subsequent NH3-SCR reaction.

关键词

Keywords

references

0

浏览量

14

下载量

0

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

相关文章

煅烧温度对Ca1-xPrMnO粉体结构与导电性能的影响

pH对掺杂Zn纳米Ni(OH)电化学性能的影响

沸石负载Mn,N共掺杂TiO2及光催化性能

直流复合绝缘子电场和覆冰相互影响机制分析

采用FD约束迁移生成虚拟样本的动液面预测

相关作者

付秋月

郝素娥

孟宪伟

李佳龙

李云娇

赵力

刘志豪

王博

相关机构

哈尔滨工业大学理学院

哈尔滨工业大学化工学院

哈尔滨工业大学化工与化学学院

北京卫星环境工程研究所可靠性与环境工程技术重点实验室

哈尔滨工业大学材料科学与工程学院

AI问答

地址：北京市丰台区顺八条1号院2号楼北阳晨光大厦2层邮编：100079
联系电话：（010）53879206 Email：tmw@bjxintong.com.cn
技术支持由北京北大方正电子有限公司提供京ICP备09082226号-64 京公网安备11010602201714号
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰