碱激发矿渣陶粒混凝土空心砌块砌体抗剪试验

更新时间：2026-10-19

- 碱激发矿渣陶粒混凝土空心砌块砌体抗剪试验
- Experimental study on shear performance of alkali-activated slag ceramsite concrete hollow block masonry
- 哈尔滨工业大学学报 2018年50卷第12期页码：165-170
- 作者机构：
  
  1. 哈尔滨工业大学土木工程学院,哈尔滨,150090
  2. 结构工程灾变与控制教育部重点实验室(哈尔滨工业大学),哈尔滨,150090
  3. 土木工程智能防灾减灾工业和信息化部重点实验室(哈尔滨工业大学),哈尔滨,150090
- 作者简介：
  
  郑文忠(1965—)，男，博士生导师, 长江学者特聘教授
- 基金信息：
  
  国家自然科学基金(51478142)
- DOI：10.11918/j.issn.0367-6234.201806062
  中图分类号： TU375.6
- 纸质出版：2018
- 稿件说明：
移动端阅览
郑文忠, 焦贞贞, 王英, 等. 碱激发矿渣陶粒混凝土空心砌块砌体抗剪试验[J]. 哈尔滨工业大学学报, 2018,50(12):165-170.

ZHENG Wenzhong, JIAO Zhenzhen, WANG Ying, et al. Experimental study on shear performance of alkali-activated slag ceramsite concrete hollow block masonry[J]. 2018, 50(12): 165-170.
郑文忠, 焦贞贞, 王英, 等. 碱激发矿渣陶粒混凝土空心砌块砌体抗剪试验[J]. 哈尔滨工业大学学报, 2018,50(12):165-170. DOI： 10.11918/j.issn.0367-6234.201806062.

ZHENG Wenzhong, JIAO Zhenzhen, WANG Ying, et al. Experimental study on shear performance of alkali-activated slag ceramsite concrete hollow block masonry[J]. 2018, 50(12): 165-170. DOI： 10.11918/j.issn.0367-6234.201806062.

摘要

为研究碱激发矿渣陶粒混凝土空心砌块砌体的受剪性能

对108个用Mb25~Mb130碱激发矿渣净浆和用Mb25~Mb80碱激发矿渣陶砂砂浆砌筑的碱激发矿渣陶粒混凝土空心砌块砌体进行抗剪试验.试验结果表明:碱激发矿渣净浆作砌筑浆体的砌体抗剪强度低于碱激发矿渣陶砂砂浆作砌筑浆体的砌体.碱激发矿渣陶砂砂浆作砌筑浆体的砌体抗剪强度低于用水泥砂浆和混合砂浆作砌筑浆体的砌体.砌体的抗剪强度随砌筑浆体抗压强度的提高而增大

Na2O含量、砂灰比对砌体抗剪强度的影响不容忽视.基于试验结果

分别建立了用碱激发矿渣净浆和碱激发矿渣陶砂砂浆作砌筑浆体时的碱激发矿渣陶粒混凝土空心砌块砌体抗剪强度计算公式.

Abstract

To investigate the shear performance of alkali-activated slag ceramsite concrete hollow block masonry

tests on 108 masonry prisms with Mb25~Mb130 of alkali-activated slag paste and Mb25~Mb80 of alkali-activated slag mortar with pottery sand were carried out. The results show that the shear strength of masonry with alkali-activated slag paste was less than that with alkali-activated slag mortar

and the shear strength of masonry with alkali-activated slag mortar was lower than that with ordinary cement and composite mortars

respectively. The shear strength of masonry increased as the compressive strength of alkali-activated slag paste and mortar increased. The effects of Na2O contents and sand to cementitious materials ratios on the shear strength of masonry should not be ignored. Based on the results

the formulae for the shear strength of alkali-activated slag ceramsite concrete hollow block masonry with alkali-activated slag pastes and mortars were developed

respectively.

关键词

Keywords

references

浏览量

333

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

考虑结构性影响的天然软黏土弹塑性本构模型

固化淤泥破碎重塑后抗剪强度及孔隙结构变化规律

碱激发矿渣陶砂砂浆砌筑的砌体弯曲受拉性能试验

不同形式生物液加固砂土试验及机理分析

多元处理情景下的异质性处理效应估计方法