Ti元素对CrTeCoNiTix高熵合金组织及性能的影响

材料科学与工程 | 更新时间：2026-08-31

- Ti元素对CrTeCoNiTix高熵合金组织及性能的影响
- Effects of Ti Addition on Microstructure and Performance of CrTeCoNiTix High Entropy Alloys
- 哈尔滨理工大学学报 2018年23卷第3期页码：149-152
- 作者机构：
  
  哈尔滨理工大学应用科学学院,黑龙江,哈尔滨,150080
- 作者简介：
- 基金信息：
- DOI：10.15938/j.jhust.2018.03.026
  中图分类号： TG132
- 纸质出版：2018
- 稿件说明：
移动端阅览
姜越, 程思梦, 祖红梅. Ti元素对CrTeCoNiTix高熵合金组织及性能的影响[J]. 哈尔滨理工大学学报, 2018,23(3):149-152.

JIANG Yue, CHENG Si-meng, ZU Hong-mei. Effects of Ti Addition on Microstructure and Performance of CrTeCoNiTix High Entropy Alloys[J]. 2018, 23(3): 149-152.
姜越, 程思梦, 祖红梅. Ti元素对CrTeCoNiTix高熵合金组织及性能的影响[J]. 哈尔滨理工大学学报, 2018,23(3):149-152. DOI： 10.15938/j.jhust.2018.03.026.

JIANG Yue, CHENG Si-meng, ZU Hong-mei. Effects of Ti Addition on Microstructure and Performance of CrTeCoNiTix High Entropy Alloys[J]. 2018, 23(3): 149-152. DOI： 10.15938/j.jhust.2018.03.026.

摘要

摘要:为了研究Ti元素对高熵合金的组织和性能的影响，采用放电等离子烧结方法制备了CrTeCoNiTix（x=0.2

0.4

0.6

0.8

1.0）多组元高熵合金。用OM、XRD和SEM等技术分析了合金的微观组织，测试了CrTeCoNiTix高熵合金的硬度、压缩强度及耐腐蚀性能。研究结果表明：不同Ti含量的高熵合金组织形态简单，物相主要为面心立方相。随着Ti含量的增加，高熵合金硬度逐渐增加，最大值达到672.59HV；压缩强度也随之增加，最大值为690.28MPa。在H2SO4中的耐腐蚀性随Ti含量增加而降低。

Abstract

Abstract:In order to explore the influence of the Ti element on the microstructure and mechanical properties of high entropy alloys(HEA)

using spark plasma sintering(SPS) method synthesize CrFeCoNiTix (x=0.2

0.4

0.2

0.4

1.0) more ingredients of HEA. Using OM

XRD and SEM techniques to explore the microstructure of the alloy

and tested the hardness

compression strength and corrosion resistance. Research has shown that the high entropy of different content of Ti alloy have the simple organization form

face centered cubic is the main solid solution phase. With increasing Ti content

the hardness of HEA increases and the maximum hardness is 672.59HV; High entropy alloys compression strength also increases

the maximum value is 690.28MPa. The corrosion resistance of HEA decreased with increasing Ti content in H2SO4.

关键词

Keywords

references

浏览量

356

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

不同温度环氧纳米复合材料击穿机制

连续结构分布动载荷的离散等效加载方法

压气机机匣内表面几何公差故障点定位

基于近场动力学的微结构铣刀破损预测与优化设计

Banach 空间中 Von Neumann-Jordan 常数型的新常数