反应合成层状多孔TiAl复合板材的组织演变

材料科学与工程 | 更新时间：2026-08-31

- 反应合成层状多孔TiAl复合板材的组织演变
- Microstructure of Layered Porous TiAl Composite Sheet Synthesized by Reacted Sintering
- 哈尔滨理工大学学报 2019年24卷第5期页码：34-38
- 作者机构：
  
  哈尔滨理工大学材料科学与工程学院,黑龙江,哈尔滨,150040
- 作者简介：
- 基金信息：
- DOI：1015938/jjhust201905007
  中图分类号： [TB331]
- 纸质出版：2019
- 稿件说明：
移动端阅览
李学问, 刘刚, 索转霞, 等. 反应合成层状多孔TiAl复合板材的组织演变[J]. 哈尔滨理工大学学报, 2019,24(5):34-38.

LI Xuewen, LIU Gang, SUO Zhuanxia, et al. Microstructure of Layered Porous TiAl Composite Sheet Synthesized by Reacted Sintering[J]. 2019, 24(5): 34-38.
李学问, 刘刚, 索转霞, 等. 反应合成层状多孔TiAl复合板材的组织演变[J]. 哈尔滨理工大学学报, 2019,24(5):34-38. DOI： 1015938/jjhust201905007.

LI Xuewen, LIU Gang, SUO Zhuanxia, et al. Microstructure of Layered Porous TiAl Composite Sheet Synthesized by Reacted Sintering[J]. 2019, 24(5): 34-38. DOI： 1015938/jjhust201905007.

摘要

以纯Ti箔、纯Al粉、纯Nb粉为原材料，首先采用粉末冶金工艺制备AlNb复合箔材，再采用箔箔冶金工艺制备层状多孔TiAl合金板材。研究结果表明：真空热压后，Ti/AlNb复合板材无新相生成，Ti箔与AlNb复合箔材结合方式为机械结合，板材厚度均匀。分步热处理后的薄板由Al3Nb、TiAl3、TiAl2、TiAl、AlNb2和Ti3Al六种相层组成，其中TiAl相层厚度约为100 μm，Ti3Al相层厚度约为12 μm，(Ti

Nb)Al3相层厚度约为80 μm，TiAl2相层厚度约为2 μm。AlNb2分布于(Ti

Nb)Al3相层中，并在(Ti

Nb)Al3相层中形成了不规则分布的孔洞。

Abstract

In this paper

pure Ti foil

pure Al powder and pure Nb powder are used as raw materials Firstly

AlNb composite foil was prepared by powder metallurgy process

and then layered porous TiAl alloy sheet is prepared by foil metallurgy The results show that after vacuum hot pressing

there is no new phase in the Ti/AlNb composite sheet

and the combination of Ti foil and AlNb composite foil is mechanically combined

and the thickness of the sheet is uniform The thin plate after step heat treatment is composed of six phase layers of Al3Nb

TiAl3

TiAl2

TiAl

AlNb2 and Ti3Al

wherein the TiAl phase layer has a thickness of about 100 μm

the Ti3Al phase layer has a thickness of about 12 μm

and the (Ti

Nb) Al3 phase layer thickness It is about 80 μm and the thickness of the TiAl2 phase layer is about 2 μm AlNb2 is distributed in the (Ti

Nb)Al3 phase layer

and irregularly distributed pores are formed in the (Ti

Nb)Al3 phase layer

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

铁水氧含量快速检测法评价球墨铸铁球化效果

SiC/SiC陶瓷基复合材料SLS/PIP 制备工艺及弯曲性能

一类病毒自发变异时滞SIR传染病模型稳定性分析

无失效数据下ZZ分布的可靠性分析

W-hyperbolic空间中的β性质